Effect of Refining and Modification on Microstructure and Properties of Recycled ADC10 Aluminum Alloy

作　　者：付亚城 董晓琼 闫俊 杨镇江 FU Ya-cheng;DONG Xiao-qiong;YAN Jun;YANG Zhen-jiang(Foshan Chenhui Metal Technology Co.,Ltd.,Foshan Guangdong 528200;Foshan Nanhai Chong Lee Non-ferrous Metal Products Co.,Ltd.,Foshan Guangdong 528225;Guangdong Hongbang Metal Aluminum Co.,Ltd.,Guangzhou Guangdong 511340)

机构地区：[1]佛山市辰辉金属科技有限公司,广东佛山528200 [2]佛山市南海创利有色金属制品有限公司,广东佛山528225 [3]广东鸿邦金属铝业有限公司,广东广州511340

出　　处：《世界有色金属》2023年第16期138-140,共3页World Nonferrous Metals

摘　　要：采用光学显微镜和拉力试验机,研究了复合细化变质对再生ADC10铝合金显微组织与力学性能的影响。结果表明:通过复合细化变质使再生ADC10铝合金的α-Al晶粒从粗大的树枝状转变为细小均匀的等轴状,使共晶Si相和富Fe相从粗大的针片状转变为细小的纤维状和颗粒状,可显著提高再生ADC10铝合金的力学性能。与未细化变质相比,细化变质后再生ADC10铝合金的抗拉强度为289.2MPa,断后伸长率为7.8%,抗拉强度提高了16.7%,断后伸长率提高了52.9%。The effects of refining and modification on the microstructure and mechanical properties of recycled ADC10 aluminum alloy were studied by means of optical microscope and tensile testing machine.The results show that the mechanical properties of the recycled ADC10 aluminum alloy can be improved significantly by adding grain refiner and modifier.The tensile strength of the recycled ADC10 aluminum alloy with refining and modification is 289.2 MPa,and the elongation after fracture is 7.8%.The tensile strength is increased by 16.7%and the elongation is increased by 52.9%compared with that of the recycled ADC10 aluminum alloy without refining and modification.

关 键 词：再生铝合金 ADC10铝合金 晶粒细化剂 变质剂 