制备工艺对W-10Ti合金组织的影响  

Effect of Preparation Technology on Microstructure of W-10Ti Alloy

作　　者：杨亚飞 吕宏军[1] 姚草根[1] 李圣刚[1] 王思伦 YANG Yafei;LYU Hongjun;YAO Caogen;LI Shenggang;WANG Silun(Aerospace Research Institute of Materials&Processing Technology,Beijing 100076)

机构地区：[1]航天材料及工艺研究所,北京100076

出　　处：《宇航材料工艺》2023年第5期38-43,共6页Aerospace Materials & Technology

摘　　要：制备了W-10Ti合金,研究了冷等静压(CIP)压力、热等静压(HIP)温度、高温处理对W-10Ti合金组织的影响。发现CIP能明显提高装料密度,有利于后续的HIP成形和元素扩散。提高CIP压力和HIP温度,能提高W与Ti扩散程度,HIP在1300℃时,纯Ti相完全消除。高温处理温度为1300、1400、1500、1700℃时,富Ti相含量先降低再升高,在1400℃时降至最低,为5.18%。在超过1400℃处理时,富Ti相会发生共析转变。W-10Ti alloy was prepared,and the effects of cold isostatic pressing(CIP)pressure,hot isostatic pressing(HIP)temperature and high temperature treatment on the microstructure are studied.It is found that CIP can significantly increase the charge density,which is beneficial to HIP forming and element diffusion.The diffusion of W and Ti can be improved by increasing CIP pressure and HIP temperature.At HIP1300℃,pure Ti phase is completely eliminated.When the high temperature treatment temperature is 1300,1400,1500 and 1700℃,the content of Ti-rich phase decreases first and then increases,and reaches the lowest at 1400℃,which is 5.18%.When treated at more than 1400℃,the Ti-rich phase underwent eutectoid transformation.

关 键 词：W-10Ti 合金 等静压 富Ti相 

分 类 号：TG14[一般工业技术—材料科学与工程]