顶吹炉炼锡氮氧化物的产生及控制实践  

Production and Control Measures of Tin Nitric Oxide Smelting by Top-blow Converter

作　　者：严航 白金龙 袁海滨 YAN Hang;BAI Jin-long;YUAN Hai-bin(Tin Industry Branch Company,YunTin Co.,Ltd.,Gejiu,Yunnan 661000,China)

机构地区：[1]云南锡业股份有限公司锡业分公司,云南个旧661000

出　　处：《云南冶金》2023年第5期80-84,共5页Yunnan Metallurgy

基　　金：云南省科技厅技术创新人才资助项目(202205AD160028)。

摘　　要：针对锡顶吹炉熔炼过程中氮氧化物的主要影响因素及产生机理,结合生产实际,通过调整工艺参数、结合脱硝工艺,提出控制氮氧化物的措施。实践证明:在炉渣硅酸度控制在1.3~1.4、熔点(1050~1150)℃、炉内温度(1050~1150)℃、保持炉内还原气氛,过程渣含锡小于20%、控制二、三次补风量≤3000Nm^(3)/h等条件下可降低N_(X)O_(Y)的生成。It mainly introduced the main influcnce factors and production mechanism of nitric oxide in the smelting process of tin top-blow furnace.Combined with the production practice,nitric oxide control measures were proposed through process parameters adjustment and denitration process.Practice shows:when the silicate degree of furnace slag was controlled at 1.3~1.4,melting point was controlled in(1050~1150)℃,The inner temperature inside the furnace was controlled at(1050~1150)℃ to keep the reduction atmosphere,process slag's tin content was less than 20%,the makeup air of the second and third times ≤3000 Nm^(3)/h and so on,production of NXOY can be decreased with the same conditions.

关 键 词：锡 顶吹炉 还原熔炼 氮氧化物 烟气脱硝 

分 类 号：TF814[冶金工程—有色金属冶金]