高能球磨+硼/碳热还原法制备(Ti,Mo,Nb,Ta,Zr)B_(2)高熵陶瓷粉末的研究  被引量:1

Study on Preparation of(Ti,Mo,Nb,Ta,Zr)B_(2) High-Entropy Ceramic Powder by High-Energy Ball Milling and Boro/Carbothermal Reduction Method

在线阅读下载全文

作  者:曾守君 金永中 吴翔[3] 苏伟 唐鑫 ZENG Shou-jun;JIN Yong-zhong;WU Xiang;SU Wei;TANG Xin(School of Materials Science and Engineering,Sichuan University of Science and Engineering,Zigong 643000,China;Material Corrosion and Protection Key Laboratory of Sichuan Province,Zigong 643000,China;Zigong Cemented Carbide Co.,Ltd.,Zigong 643011,China)

机构地区:[1]四川轻化工大学材料科学与工程学院,四川自贡643000 [2]材料腐蚀与防护四川省重点实验室,四川自贡643000 [3]自贡硬质合金有限责任公司,四川自贡643011

出  处:《稀有金属与硬质合金》2023年第6期47-52,共6页Rare Metals and Cemented Carbides

基  金:四川省科技厅重点研发计划项目(20ZDYF2629);四川轻化工大学研究生创新基金项目(Y2022003)。

摘  要:以TiO_(2)、MoO_(3)、Nb_(2)O_(5)、Ta2O5、ZrO_(2)、B_(4)C和炭黑为原料,采用高能球磨+硼/碳热还原法制备(Ti,Mo,Nb,Ta,Zr)B2高熵陶瓷粉末,并借助XRD、SEM等手段对反应产物的物相组成和微观形貌进行了表征。实验结果表明:球磨时间、还原温度和保温时间是制备高品质(Ti,Mo,Nb,Ta,Zr)B_(2)高熵陶瓷粉末的重要影响因素。当球磨时间为2h、真空碳热还原温度为1700℃、保温2h时,可制备出粒径约为1~2μm、元素分布均匀且具有单一相成分的高品质(Ti,Mo,Nb,Ta,Zr)B_(2)高熵陶瓷粉末。Using TiO_(2),MoO_(3),Nb_(2)O_(5),Ta_(2)O_(5),ZrO_(2),B_(4)C and carbon black as raw materials,(Ti,Mo,Nb,Ta,Zr)B_(2) high-entropy ceramic powder was prepared by high-energy ball milling and boro/carbothermal reduction method,with the phase composition and microstructure of the reaction products being characte-rized by XRD and SEM.The results show that ball milling time,reduction temperature,and holding time are important factors for the preparation of high-quality(Ti,Mo,Nb,Ta,Zr)B_(2) high-entropy ceramic powder.The high-quality(Ti,Mo,Nb,Ta,Zr)B_(2) high-entropy ceramic powder can be prepared with particle size of 1~2μm,uniform distribution of elements,and single phase composition under the conditions of ball milling time of 2 h,vacuum carbothermal reduction temperature of 1700℃,and holding time of 2 h.

关 键 词:(Ti Mo Nb Ta Zr)B_(2) 高熵陶瓷粉末 高能球磨 硼/碳热还原 微观结构 

分 类 号:TG132.3[一般工业技术—材料科学与工程]

 