Synthesis and Properties of PBT-b-PTMG Block Copolymers with Different Soft and Hard Segment Contents

作　　者：王杰[1] 邢喜全 何肖 王秀华[1] JieWang;Xiquan Xing;Xiao He;XiuhuaWang(National Engineering Lab of Textile Fiber Materials and Processing Technology,Zhejiang Sci-Tech University,Hangzhou 310018,China;Yuyao Dafa Chemical Fiber Co.,Ltd.,Ningbo 315400,China)

机构地区：[1]浙江理工大学纺织纤维材料与加工技术国家地方联合工程实验室,浙江杭州310018 [2]余姚大发化纤有限公司,浙江宁波315400

出　　处：《高分子材料科学与工程》2023年第9期27-34,共8页Polymer Materials Science & Engineering

基　　金：科技创新2025重大专项(宁波市重大科技任务攻关项目)(2022Z156)。

摘　　要：采用直接酯化熔融缩聚法合成一系列不同软硬段含量的聚对苯二甲酸丁二醇酯(PBT)-b-聚四氢呋喃(PTMG)聚醚酯嵌段共聚物(TPEE),以红外光谱、核磁共振、X射线衍射、差示扫描量热分析和动态力学热分析等方法,探讨不同软硬段质量比及不同软段相对分子质量对材料结构及相对分子质量、热性能和黏弹性等的影响。结果表明,在相同出料功率下制得的TPEE的特性黏度均高于PBT,并随硬段质量分数或软段相对分子质量的增大而减小;TPEE的熔点下降幅度随软段摩尔分数的增加而增大;TPEE中存在微相分离结构,当硬段质量分数为60%、软段PTMG数均分子量为2×103时,同时出现了分别代表硬段PBT以及软段中PTMG的玻璃化转变的损耗角正切峰。研究结果为TPEE的合成和应用提供了一定借鉴。A series of polybutylene terephthalate(PBT)-b-polytetrahydrofuran(PTMG)polyether ester block copolymers(TPEE)with different soft and hard segment contents were synthesized by direct esterification melt polycondensation.The effects of different soft and hard segment mass ratios and soft segment molecular weight on the structure,molecular weight,thermal properties and viscoelasticity of the materials were investigated by FT-IR,1H-NMR,XRD,DSC and DMA.The results show that the characteristic viscosity of TPEE is higher than that of PBT at the same discharge power,and decreases with the increase of the mass fraction of hard section or molecular weight of soft section;the decrease of its melting point increases with the increase of the molar fraction of soft section;the micro-phase separation structure exists in TPEE,when the mass fraction of hard section is 60%,and the number-average molecular weight of soft section is 2×10^(3),and the loss angle tangent peaks representing the glass transition of PBT in hard segment and PTMG in soft segment respectively appear.The results of the study provide some reference for the synthesis and application of TPEE.

关 键 词：直接酯化 软硬段含量 嵌段共聚物 黏弹性 微相分离 玻璃化转变 

分 类 号：TQ334[化学工程—橡胶工业]