静电纺MnO_(2)/CNFs纤维及对铬黑T的吸附性能  

Preparation of Electrospun MnO_(2)/CNFs Fibers and Their Adsorption Performance for Chromium Black T

作　　者：艾刚刚 沙夜龙 马宝权 边海龙 王娟 Ai Ganggang;Sha Yelong;Ma Baoquan;Bian Hailong;Wang Juan(Yan'an Oil and Gas Product Quality Inspection and Testing Co.,Ltd.,Yan′an 716000,China;National Petroleum and Natural Gas Product Quality Supervision and Inspection Center(Yan′an),Yan′an 716000,China)

机构地区：[1]延安油气产品质量检验检测有限责任公司,陕西延安716000 [2]国家石油天然气产品质量监督检验中心(延安),陕西延安716000

出　　处：《山东化工》2023年第21期60-62,共3页Shandong Chemical Industry

摘　　要：以醋酸锰和聚丙烯腈为原料,采用静电纺丝法制备了MnO_(2)/CNFs复合纤维,研究了染料的种类、染料初始浓度、煅烧温度、吸附时间等因素对该复合纤维吸附染料性能的影响。当铬黑T初始质量浓度为30 mg/L,醋酸锰与PAN质量比为40%,煅烧温度为900℃时,吸附时间为2.5 h,温度为40℃时,该复合材料对铬黑T的吸附量为18.31 mg/g,去除率达到61.04%。MnO_(2)/CNFs composite fibers were prepared by electrospinning method using manganese acetate and polyacrylonitrile as raw materials.Then the effects of dyes,initial concentration of dyes,calcination temperature,adsorption time and other factors on the adsorption performance of the composite fibers were studied.When the initial concentration of chromium black T was 30 mg/L,the mass ratio of manganese acetate to PAN was 40%,the calcining temperature was 900℃,the adsorption time was 2.5 h,and the temperature was 40℃,the adsorption capacity was 18.31 mg/g,and the removal rate is 61.04%.

关 键 词：静电纺丝 二氧化锰 有机染料 吸附 