Gas release characteristics during carbonization of iron coke hot briquette and influence of heating rate  

作　　者：Zi-yu Wang Dong Han Zheng-gen Liu Man-sheng Chu Yong-jie Zhang Li-feng Zhang Ji-wei Bao Ming-yu Wang 

机构地区：[1]School of Metallurgy,Northeastern University,Shenyang,110819,Liaoning,China [2]Engineering Research Center of Frontier Technologies for Low-Carbon Steelmaking(Ministry of Education),Shenyang,110819,Liaoning,China [3]Liaoning Province Engineering Research Center for Technologies of Low-Carbon Steelmaking,Shenyang,110819,Liaoning,China

出　　处：《Journal of Iron and Steel Research International》2023年第11期2163-2172,共10页

摘　　要：The release characteristics of CH_(4),H_(2),CO and CO_(2) from iron coke hot briquette(ICHB)during carbonization were studied.The results show that compared with briquette without iron ore,Fe_(3)O_(4) can inhibit the release rate of H2 and promote the production of CO and CO_(2).In addition,when the heating rate increases from 3 to 7℃/min,the release rates of CH4 and H2 increase,while the release rates of CO and CO_(2) first increase and then decrease.The carbonization process of ICHB was segmented,and corresponding kinetic analysis was carried out.The results show that the activation energy of StageⅡand StageⅣis higher in the carbonization process of ICHB,and the active pyrolysis of coal and the reduction of iron ore occur in these two stages.In addition,the effect of heating rate on the kinetic parameters of ICHB carbonization process was investigated.It was found that when the heating rate increased,the reaction activation energy of StageⅣdecreased first and then increased,which was consistent with the release law of CO and CO_(2).The analysis showed that the increase in heating rate leads to more reactions at higher temperatures,resulting in an increase in the release rate of some gases.In addition,thermal hysteresis can also cause some processes to fail to fully react at the end of heating.It is also found that the apparent activation energy and preexponential factor have kinetic compensation effect during the car-bonization of ICHB.

关 键 词：Iron coke hot briquette CARBONIZATION Gas release characteristic Heating rate Kinetics 