TC4钛合金扩散连接区热变形特性行为研究  

Thermal Deformation Behavior of Diffusion Bonding Region of TC4 Titanium Alloy

作　　者：杨兴远 姜沐池 任德春 蔡雨升 吉海宾[1] 雷家峰[1] 杨锐[1] Yang Xingyuan;Jiang Muchi;Ren Dechun;Cai Yusheng;Ji Haibin;Lei Jiafeng;Yang Rui(Research Department of Light and High Strength Materials,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China)

机构地区：[1]中国科学院金属研究所轻质高强材料研究部,辽宁沈阳110016

出　　处：《稀有金属材料与工程》2023年第12期4125-4132,共8页Rare Metal Materials and Engineering

基　　金：工信部民机专项(MJZ 2-2N21-5)。

摘　　要：以TC4钛合金扩散连接区为研究对象,在变形温度920、950、980、1010℃及应变速率0.01、0.1、1、10 s^(-1)的条件下进行热变形试验,研究了变形温度和应变速率对TC4钛合金扩散连接区流变应力和微观组织的影响规律。结果表明:TC4钛合金扩散连接区在高温下具有明显的动态软化特征,流变应力随变形温度的升高而降低,随变形速率的提高而增大;高温变形后扩散连接界面消失,随变形温度的升高,等轴α相的体积分数减少,同时伴有短棒状和板条状的次生α相出现,且次生α相的体积分数随应变速率增加逐渐降低;当变形温度达到1010℃时,出现马氏体α′相;以双曲正弦形式修正的Arrhenius方程为基础,建立了TC4钛合金扩散连接区双曲正弦本构方程以及热加工图,确定TC4钛合金扩散连接区的最佳变形温度为920~950℃,变形速率为0.01~0.1 s^(-1)。The thermal deformation tests on the diffusion bonding region of TC4 titanium alloy were conducted at deformation temperature of 920,950,980,1010℃and the strain rate of 0.01,0.1,1,10 s^(-1).The effects of deformation temperatures and strain rates on the flow stress and microstructure of diffusion-bonded region of TC4 titanium alloy were investigated.Results show that the diffusion bonding region of TC4 titanium alloy has obvious dynamic softening characteristics at high temperature,and the flow stress is decreased with increasing the deformation temperature and it is increased with increasing the deformation strain rate.The diffusion bonding interface disappears after high temperature deformation,and the volume fraction of isoaxialαphase is decreased with increasing the deformation temperature.Short rod-like and plate-like secondaryαphase also appears.Besides,the volume fraction of secondaryαphase is decreased with increasing the strain rate.When the deformation temperature reaches 1010℃,the martensiteα'phase appears.Based on the hyperbolic sinusoidal modified Arrhenius equation,the hyperbolic sinusoidal constitutive equation and the thermal processing diagram of diffusion bonding region of TC4 titanium alloy were established.The optimal deformation parameters of diffusion bonding region of TC4 titanium alloy are determined as T=920-950℃and 1ε0.01-0.1 s-=.

关 键 词：TC4钛合金 扩散连接 高温变形 本构方程 热加工图 

分 类 号：TG146.23[一般工业技术—材料科学与工程]