聚对苯二甲酸乙二醇酯(PET)膜用透明耐高温防黏涂层的制备及性能研究  

Preparation and Properties of Transparent High Temperature Resistant and Anti-sticking Coating for PET Film

作　　者：曲一凡 安秋凤[1] 焦岚姣 王召帅 Qu Yifan;An Qiufeng;Jiao Lanjiao;Wang Zhaoshuai(Shaanxi Key Laboratory of Chemical Additives for Industry,Shaanxi University of Science and Technology,Xi'an 710021,China)

机构地区：[1]陕西科技大学陕西省轻化工助剂重点实验室,西安710021

出　　处：《涂料工业》2024年第2期29-36,44,共9页Paint & Coatings Industry

基　　金：陕西省重点研发计划项目(2020ZDLGY13-11)。

摘　　要：以三氟丙基三甲基环三硅氧烷(D_(3)F)、八甲基环四硅氧烷(D_(4))、四甲基二氢二硅氧烷(D_(2)^(H))为原料,经开环缩聚、硅氢加成、水解共缩聚反应制得了一种有机-无机杂化改性氟硅树脂(AFPS@SiO_(2)),将其涂覆于PET膜表面,制得透明耐高温防黏涂层。通过红外光谱仪(FT-IR)、扫描电镜(SEM)、X射线光电子能谱仪(XPS)、热重分析仪(TGA)对目标产物的结构、形貌及性能进行表征测试,讨论了分子链节物质的量比[n(D)∶n(DF)]对涂层水接触角、剥离力、附着力、硬度和透光率的影响。结果表明:当n(D)∶n(DF)=3∶2时,防黏涂层的综合性能最优,其水接触角为108.1°,剥离力为0.029 N/cm,附着力为1级,硬度为4H,透光率为90.0%。提供了一种PET膜用透明耐高温防黏涂层的制备思路,为后续研究提供了参考。A organic-inorganic hybrid modification fluorosilicone resin(AFPS@SiO_(2))was prepared by ring-opening polycondensation,hydrosilylation and hydrolytic copolycondensation of 1,3,5-tris(3,3,3-trifluoropropyl)methylcyclotrisiloxane(D_(3)F),octamethyl-cyclotetrasiloxane(D_(4)),and 1,1,3,3-tetramethyldisiloxane(D_(2)^(H)).Then AFPS@SiO_(2) was applied to the surface of PET film to construct a transparent high temperature resistant and anti-sticking coating.The structure,morphology,and properties of the production were characterized by FT-IR,SEM,XPS and TGA.The effects of the molar ratio[n(D)∶n(DF)]on the water contact angle,peeling force,adhesion,hardness and light transmittance of the coating were discussed.The results show that when the molar ratio[n(D)∶n(DF)]was 3∶2,the comprehensive performance of the anti-sticking coating was the best. Its water contact angle was 108. 1°,peeling force was 0. 029 N/cm,the adhesion wasgrade 1,the hardness was 4H,and light transmittance was 90. 0%. This study provided apreparation idea of transparent high temperature resistant and anti-sticking coating for PETfilm,which indicated certain application value.

关 键 词：防黏涂层 硅氢加成 含氟聚硅氧烷 剥离力 PET膜 透明 耐高温 

分 类 号：TQ637.2[化学工程—精细化工]