蒸压轻质混凝土板专用粘结砂浆的制备与性能研究  

Preparation and performance study of binder mortar for autoclaved lightweight concrete slabs

作　　者：单俊鸿[1] 史圣然 王荣荣 李春 张景华 SHAN Junhong;SHI Shengran;WANG Rongrong;LI Chun;ZHANG Jinghua(School of Civil Engineering,Hebei University of Engineering,Handan 056038,China;Wuhan Deyi Environmental Protection New Material Co.Ltd.,Wuhan 430200,China;The Second Construction Limited Company of China Construction Eighth Engineering Division,Jinan 250014,China)

机构地区：[1]河北工程大学土木工程学院,河北邯郸056038 [2]武汉德毅环保新材料有限公司,湖北武汉430200 [3]中建八局第二建设有限公司,山东济南250014

出　　处：《新型建筑材料》2024年第2期48-53,共6页New Building Materials

基　　金：中央引导地方科技发展专项资金项目(YDZX20181400002774)。

摘　　要：采用P·O42.5水泥、粉煤灰、石灰石超细粉、矿粉以及外加剂为原料制备水泥基粘结砂浆。采用正交试验确定水泥基胶凝材料的最优配合比,研究淀粉醚对纤维素醚取代率和膨胀剂对水泥基粘结砂浆的性能影响,并利用XRD和SEM分析水化产物和微观形貌,研究外加剂的作用机理。结果表明,m(水泥)∶m(粉煤灰)∶m(矿粉)∶m(石灰石超细粉)=22∶4∶4∶5时,水泥基胶凝材料的性能最优;淀粉醚适量取代纤维素醚可以增强砂浆保水性,提高砂浆强度,减少收缩;少量膨胀剂可以提高砂浆的早期强度,增加掺量则降低早期强度,提高砂浆后期强度。制备的水泥基粘结砂浆符合JC/T 890—2017《蒸压加气混凝土墙体专用砂浆》的要求。P·O42.5 cement,fly ash,limestone superfine powder,mineral powder and admixtures were used as raw materials to prepare cementitious mortar.The orthogonal test was used to determine the optimum ratio of cement-based cementitious materials,and the effects of starch ether on cellulose ether substitution rate and expansion agent on the performance of cementitious mortar were investigated,the hydration products and microscopic morphology were analyzed by XRD and SEM respectively,and the mechanism of action of additives was studied.The results showed that the performance of cement-based cementitious materials was opti-mal when the mass ratio of cement,fly ash,mineral powder and limestone ultrafine powder was 22 ∶4∶4∶5;the appropriate amount of starch ether instead of cellulose ether could enhance the water retention of mortar,increase the strength of mortar and improve the shrinkage;a small amount of expansive agent could improve the early strength of mortar,and an increased amount of admixture could reduce the early strength and improve the later strength of mortar.The finally prepared cement-based bonded mortar meet the requirements of JC/T 890—2017 "Special Mortar for Autoclaved Aerated Concrete Wall".

关 键 词：粘结砂浆 正交试验 矿物掺合料 纤维素醚 淀粉醚 膨胀剂 