Color and Gloss Changes of a Lignin-Based Polyurethane Coating under Accelerated Weathering  

作　　者：Fatemeh Hassani Khorshidi Saeed Kazemi Najafi Farhood Najafi Antonio Pizzi Dick Sandberg Rabi Behrooz 

机构地区：[1]Department of Wood Science and Technology,Faculty of Natural Resources,Tarbiat Modares University,Tehran,Iran [2]Department of Resin and Additives,Institute for Color Science and Technology,P.O.Box 16765-654,Tehran,Iran [3]LERMAB,University of Lorraine,Blvd des Aiguillettes,Nancy,54000,France [4]Wood Science and Engineering,LuleåUniversity of Technology,Skellefteå,Sweden

出　　处：《Journal of Renewable Materials》2024年第2期305-323,共19页可再生材料杂志（英文）

摘　　要：The purpose of this research study was to investigate the properties of polyurethane coatings based on lignin nano-particles.For this purpose,the prepared coatings were applied to pine wood surfaces and weathered artificially.Subsequently,color and gloss of the coatings were measured before and after the weathering test.Field emission scanning electron microscopy(FE-SEM)micrographs prepared from the coatings showed that the average size of nano-particles in the polyurethane substrate was approximately 500 nm.Nuclear magnetic resonance(13C-NMR)spectroscopy showed that strong urethane bonds were formed in the nano-lignin-based polyurethane.Differential calorimetric analysis(DSC)test revealed that the glass-transition temperature(Tg)of lignin nanoparticles modified with diethylenetriamine(DETA)was 112.8℃ and Tg of lignin nano-particles modified with ethylenediamine(EDA)was 102.5℃,which is lower than the Tg of un-modified lignin(114.6℃)and lignin modified with DETA(126.8℃)and lignin modified with EDA(131.3℃).The coatings modified with lignin nano-particles had a greater change in gloss.The lignin nano-particles in the modified coating are trapping hydroxyl radicals which reduces photoactivity and yellowing of the polyurethane by about 3 times compared to unmodified polyurethane coatings.After weathering test,the nano-lignin-based coating had a rougher surface with a lower contact angle(0.78°)compared to the unmodified polyurethane coating(0.85°).

关 键 词：AMINATION propylene carbonate LIGNIN BIOPOLYMER polyurethane coating POLYOL UN SDG 13 

分 类 号：TQ63[化学工程—精细化工]