基于(PEA)_(2)PbBr_(4)单晶的光致发光防伪织物标贴制备与性能  

Preparation and performance of photoluminescence anti-counterfeiting fabriclabeling based on (PEA)_(2)PbBr_(4) single crystal

作　　者：胡晓亭 徐磊[1,2] 李楠 HU Xiaoting;XU Lei;LI Nan(School of Textile Science and Engineering,Tiangong University,Tianjin 300387,China;Research Institute of Keqiao District,Tiangong University,Tianjin 300387,China;Tangshan Sanyou Xingda Chemical Fiber Co.,Ltd.,Tangshan 063305,China)

机构地区：[1]天津工业大学纺织科学与工程学院,天津300387 [2]天津工业大学绍兴柯桥研究院,天津300387 [3]唐山三友兴达化纤有限公司,河北唐山063305

出　　处：《现代纺织技术》2024年第3期81-90,共10页Advanced Textile Technology

基　　金：国家自然科学基金项目(51303131)。

摘　　要：为制备高效轻质的荧光防伪织物标贴,采用反溶剂气相辅助结晶法生长不同尺寸和密度的苯乙胺溴化铅((PEA)_(2)PbBr_(4))单晶,并将其旋涂封装于PVC薄膜内,与织物热轧复合,得到具有光致发光防伪功能的织物标贴;通过XRD、SEM、紫外可见光度计和瞬态荧光光谱仪等测试对单晶的结构、复合膜与织物标贴的发光特性进行分析。结果表明:采用简单温和的工艺即可有效制备晶体并调控其尺寸和密度,制作具有防伪功能的织物标贴。尺寸为5~10μm的二维结构单晶,其厚度约200 nm;通过调节邻二氯苯与N,N-二甲基甲酰胺的溶剂比例能够有效控制(PEA)_(2)PbBr_(4)单晶尺寸。当单晶尺寸约为5μm时,其分布状态、结晶性和发光性能最为优异,其复合膜的吸收峰和发射峰分别位于391 nm和414 nm处。采用超微量的单晶防伪标贴即可在365 nm紫外光的激发下发出强烈均匀的蓝紫色光,并且,用于织物防伪能够达到洗可穿及耐磨标准,实现有效的防伪功能。The development and application of fabric security labels with identification function ensure the safety of textiles.Ultraviolet photoluminescent textiles refer to the fact that the fabric emits a specific color of light after being excited from a colorless state when it is irradiated by ultraviolet light,so as to achieve the purpose of anti-counterfeiting.Previous studies have shown that the(PEA)_(2)PbBr_(4) single crystal with ultraviolet photoluminescence performance has excellent characteristics such as high color purity and high crystallinity,and can be prepared by simple process,mild conditions and mass production.To prepare efficient and lightweight fluorescent anti-counterfeiting fabric labels,phenethylammonium bromide was prepared byβ-phenethylamine and hydrobromic acid,and it was dissolved with lead bromide at a molar ratio of 2:1 to N,N-dimethylformamide to configure a precursor solution.By adjusting the solvent ratio of o-dichlorobenzene to N,N-dimethylformamide,two-dimensional layered(PEA)_(2)PbBr_(4) single crystals of different sizes and densities were grown by anti-solvent gas-assisted crystallization.The single crystal with the best distribution and luminescence performance was selected,and the single crystal solution under this condition was spin-coated and encapsulated in a 0.1 mm thick PVC film to prepare a single crystal PVC composite film,and a fabric label with photoluminescence anti-counterfeiting function was obtained by hot rolling with the fabric.The crystallization properties,distribution,morphological structure and luminescence characteristics of single crystals and composite films and fabric labels were studied by fluorescence microscopy,laser particle size analyzer,XRD,SEM,ultraviolet-visible photometer and transient fluorescence spectrometer,and their application effects in textiles were discussed through washable wearable and wear-resistant tests.The results show that(PEA)_(2)PbBr_(4) single crystals have a series of periodically repeated,uniformly spaced and well-defined strong

关 键 词：苯乙胺溴化铅 二维钙钛矿单晶 光致发光 荧光防伪 织物标贴 纺织品防伪 

分 类 号：TS103.846[轻工技术与工程—纺织工程]