不同钢铁表面无氰镀镉钛和氰化镀镉钛镀层性能差异  

Differences in performance between cyanide free cadmium titanium plating and cyanide plated cadmium titanium plating on different steel surfaces

作　　者：郝江华 高晓颖 王浩军 段党全 詹中伟 张骐 Hao Jianghua;Gao Xiaoying;Wang Haojun;Duan Dangquan;Zhang Zhongwei;Zhang Qi(AVIC Xi’an Aircraft Industry Group Company Ltd.,Xi’an 710089,China;Aviation Key Laboratory of Science and Technology on Advanced Corrosion and Protection for Aviation Material,Beijing Institute of Aeronautical Materials,Surface Engineering Institution,Beijing 100095,China)

机构地区：[1]中航西安飞机工业集团股份有限公司,陕西西安710089 [2]中国航发北京航空材料研究院航空材料先进腐蚀与防护航空科技重点实验室,北京100095

出　　处：《电镀与精饰》2024年第4期59-65,共7页Plating & Finishing

摘　　要：在不同钢铁基体表面进行无氰镀镉钛和氰化镀镉钛,对比不同钢铁基体表面两种工艺的镀层氢脆性能、疲劳性能和拉伸性能。结果表明:300M钢和4340钢进行无氰镀镉钛和氰化镀镉钛后的氢脆性能差异不明显。300M钢和50CrVA钢进行无氰镀镉钛和氰化镀镉钛后,疲劳性能有较小的变化。50CrVA钢进行无氰镀镉钛后疲劳极限相比裸材降低了1.5%,进行氰化镀镉钛后疲劳极限相比裸材提高了5.0%;300M钢进行无氰镀镉钛后疲劳极限相比于裸材增加了3%;进行氰化镀镉钛后疲劳极限相比于裸材降低了7%。无氰电镀镉钛对300M钢和50CrVA钢基体拉伸性能影响较小,相比于裸材,各项指标数值波动均在5%以内。Cyanide free cadmium titanium plating and cyanide cadmium titanium plating were performed on the surfaces of different steel substrates,and the hydrogen embrittlement,fatigue,and tensile properties of the coatings were compared between the two processes on the surfaces of different steel substrates.The results show that there is no significant difference in hydrogen embrittlement performance between 300M steel and 4340 steel after cyanide free cadmium titanium plating and cyanide plated cadmium titanium plating.After cyanide free cadmium titanium plating and cyanide plated cadmium titanium plating on 300M steel and 50CrVA steel,there was a small change in fatigue performance.After cyanide free cadmium titanium plating on 50CrVA steel,the fatigue limit was reduced by 1.5%compared to the bare material,and after cyanide plating on cadmium titanium,the fatigue limit was increased by 5.0%compared to the bare material.After cyanide free cadmium titanium plating at 300M steel,the fatigue limit increased by 3%compared to the bare material.After cyanide plating cadmium titanium,the fatigue limit was reduced by 7%compared to bare materials.Cyanide free electroplating of cadmium titanium has little effect on the tensile properties of 300M steel and 50CrVA steel matrices,and compared to bare materials,the fluctuation of various index values is within 5%.

关 键 词：电镀镉钛 疲劳 氢脆 拉伸性能 

分 类 号：TQ153.2[化学工程—电化学工业]