极性溶剂预处理对间位芳纶染色性能和机械性能的影响  

Effect of pretreatment with polar solvent on the dyeing and mechanical properties of meta-aramid fibers

作　　者：宋吉贤 张思嘉 江华[1] SONG Jixian;ZHANG Sijia;JIANG Hua(Engineering Research Center for Eco-Dyeing&Finishing of Textiles,Ministry of Education,Zhejiang Sci-Tech University,Hangzhou 310018,China)

机构地区：[1]浙江理工大学生态染整技术教育部工程研究中心,杭州310018

出　　处：《现代纺织技术》2024年第4期76-83,共8页Advanced Textile Technology

基　　金：国家自然科学基金项目(22278377);浙江省自然科学基金项目(LY22B060005)。

摘　　要：为提升间位芳纶的可染性,采用极性有机溶剂对间位芳纶进行预处理,使用分散染料进行染色,对预处理及染色工艺条件进行优化,研究极性溶剂预处理对间位芳纶织物染色性能及机械性能的影响。结果表明:最佳的预处理工艺为使用DMSO在55℃时处理30 min,按此条件所得间位芳纶织物的断裂强力为950 N,断裂伸长率为36%,织物收缩率小于10%;最佳的染色工艺为使用偶氮型分散染料在80℃时染色60 min,此时,染料上染率达到80.9%~97.6%,染色织物耐皂洗、耐摩擦和耐升华等色牢度可以达到4级以上。使用极性溶剂在较低温预处理可有效提升间位芳纶的可染性,并显著降低机械性能损伤。Meta-aramid fibers are known to be difficult to dye because of their high crystallinity and compact structure.Pretreatment with polar organic solvents can well swell meta-aramid fibers,thus facilitating the dyeing process.Reported papers usually proceed the pretreatment at high temperature,leading to a severe fabric shrink accompanied with a remarkable decline of the mechanical property.Therefore,it is important to balance the relationship between dyeing performance and mechanical property.The aim of this paper is to explore the feasibility to decrease the fabric damage by studying the effect of pretreating/dyeing process on dyeing/mechanical properties.In this paper,the mechanical property of a meta-aramid fabric was assessed by shrinkage rate,breaking strength and elongation values,while the dyeing property was evaluated in terms of dye exhaustion,color depth as well as color fastness.The pretreating and dyeing processes were optimized.The effect of pretreating temperature and time on the mechanical property was investigated,and the effect of dyeing temperature on the dyeing performance was studied.Besides,15 disperse dyes were applied to dyeing meta-aramid fabrics at optimized pretreating and dyeing condition.Moreover,scanning electron microscope(SEM)was also used to analyze the fiber surface.Pretreatment with polar organic solvents,such as N,N-dimethylformamide(DMF),N,N-dimethylacetamide(DMAc)and dimethyl sulfoxide(DMSO)was confirmed to efficiently improve the dyeing performance of meta-aramid fabrics,while DMSO was demonstrated to be the best solvent when compared with others at the same pretreating condition.When dyeing the pretreated meta-aramid fabrics with C.I.disperse red 167,the dye exhaustion value was largely improved with the increase of the pretreating temperature and prolonging of the pretreating time.A temperature of 55℃and a time of 30 min were optimized for the pretreating process.Further investigation of the dyeing process indicated that a dyeing temperature of 80℃and a time of 60 min were

关 键 词：间位芳纶 预处理 染色性能 分散染料 机械性能 

分 类 号：TS193.8[轻工技术与工程—纺织化学与染整工程]