全固态无负极锂金属电池纳米化复合集流体构筑  

Nanocomposite Current Collectors for Anode-Free All-Solid-State Lithium Batteries

作　　者：刘泽宇 黄文泽[1] 肖阳 张俊东 孔伟进[1] 武鹏 赵辰孜 陈爱兵 张强 Zeyu Liu;Wenze Huang;Yang Xiao;Jundong Zhang;Weijin Kong;Peng Wu;Chenzi Zhao;Aibing Chen;Qiang Zhang(Beijing Key Laboratory of Green Chemical Reaction Engineering and Technology,Department of Chemical Engineering,Tsinghua University,Beijing 100084,China;Zhili College,Tsinghua University,Beijing 100084,China;Tanwei College,Tsinghua University,Beijing 100084,China;BMW China Services Ltd.,Beijing 101318,China;College of Chemical and Pharmaceutical Engineering,Hebei University of Science and Technology,Shijiazhuang 050018,China)

机构地区：[1]清华大学化学工程系,绿色化学反应工程与技术北京市重点实验室,北京100084 [2]清华大学致理书院,北京100084 [3]清华大学探微书院,北京100084 [4]宝马(中国)服务有限公司,北京101318 [5]河北科技大学化学与制药工程学院,石家庄050018

出　　处：《物理化学学报》2024年第3期60-68,共9页Acta Physico-Chimica Sinica

基　　金：国家重点研发计划(2021YFB2500300);国家自然科学基金(22108151);河北省科技项目(22344402D);博士后国际交流计划引进项目(YJ20210125)资助。

摘　　要：全固态无负极锂金属电池(AFSSLB)是一种通过初次充电形成金属锂负极的新型锂电池,它的负极与正极容量比为1,能使任意锂化正极系统达到最大能量密度。无机固态电解质的引入使无负极锂金属体系兼具高安全性。然而,电池循环过程中的锂离子通量不均导致的界面接触损失和锂枝晶生长会不断加剧,从而造成电池循环容量迅速衰减。本文构筑了纳米化的银碳复合集流体,显著增强了全固态无负极锂金属电池中集流体-电解质界面的性能。使用该集流体的固态电池循环过程中接触良好,界面阻抗为~10Ω·cm^(-2)。从而实现了超过7.0mAh·cm^(-2)锂金属的均匀稳定沉积,并在0.25mA·cm^(-2)的电流条件下实现循环200次以上。The anode-free solid-state lithium battery(AFSSLB)is a type of lithium battery that utilizes an initial charging process to generate lithium metal as the anode.With a 1:1 anode-to-cathode capacity ratio,it enables any lithiated cathode system to achieve a maximal energy density.Furthermore,the incorporation of inorganic solid electrolytes in the AFSSLB greatly enhances its intrinsic safety.However,the AFSSLB faces challenges related to interfacial issues between the electrolyte and collector.During the cycling process,uneven lithium-ion flux can result in contact loss and dendrite growth,ultimately leading to rapid battery failure.Addressing these interfacial problems is crucial for the successful implementation and performance of AFSSLBs.The absence of initial lithium metal material prevents the battery system from accommodating additional lithium through a modified anode.Instead,it relies on high Coulomb efficiency during cycling.Consequently,ensuring continuous and uniform contact at the anode interface is crucial for maintaining the reversibility of lithium deposition.Herein,a nanocomposite current collector is introduced to enhance the interface between the collector and electrolyte in AFSSLB.In this approach,silver nanoparticles are dispersed within the carbon materials to construct a composite current collector.The incorporation of the silver-carbon nanocomposite layer results in a low interfacial impedance of 10Ω·cm^(-2),indicating that the electrolyte-collector interface maintains contact throughout the charging and discharging processes.The focused ion beam(FIB)technology and electron microscopy were employed to analyze the battery cross sections,revealing that lithium metal could be deposited in a thickness of more than 25μm without short-circuiting using this silver-carbon nanocomposite current collector.The solid-state batteries equipped with nanocomposite current collectors exhibited an enhanced dissolution of silver in the lithium metal,leading to the formation of abundant lithiophilic sites.The

关 键 词：全固态电池 无负极锂金属二次电池 纳米集流体 界面接触 锂金属电池 

分 类 号：O646[理学—物理化学]