Large-Area Gravure-Printed AgNWs Electrode on Water/Oxygen Barrier Substrate for Long-Term Stable Large-Area Flexible Organic Solar Cells  

作　　者：Hao Wang Yaqin Pan Yunfei Han Zhuo Chen Tianyu Liu Lianping Zhang Qun Luo Chang-Qi Ma 

机构地区：[1]Printable Electronics Research Center & i-Lab,Suzhou Institute of Nano-Tech and Nano-Bionics,Chinese Academy of Sciences (CAS),Suzhou,Jiangsu,215123 China [2]Nano Science and Technology Institute,University of Science and Technology of China,166 Ren Ai Road,SEID SIP,Suzhou,Jiangsu,215123 China

出　　处：《Chinese Journal of Chemistry》2024年第5期478-484,共7页中国化学（英文版）

基　　金：supported by the National Natural Science Foundation of China(22135001);Youth Innovation Promotion Association(2019317);Young Cross Team Project of CAS(No.JCTD-2021-14);“Dual Carbon"Science and Technology Innovation of Jiangsu province(Industrial Prospect and Key Technology Research Program)(BE2022021);Suzhou Science and Technology Program(ST202219);CAS Special Research Assistant(SRA)Program of Suzhou Institute of Nano-Tech and Nano-Bionics(E355130101);grateful for the technical support for Jiangsu Funding Program for Excellent Postdoctoral Talent,Nano-X from Suzhou Institute of Nano-Tech and Nano-Bionics,Chinese Academy of Sciences(A2107).

摘　　要：Large-area AgNWs electrodes(25 cm×10 cm)were fabricated through roll-to-roll printing on the polyvinyl alcohol(PVA)modified water and oxygen barrier substrate.The modification of the barrier film with PVA improved the wettability of silver nanowires on the barrier films and led to the formation of homogenous large-area AgNWs networks.The mechanical flexibility,especially the adhesion force between the silver electrode and the barrier film substrate was dramatically improved through PVA modification.The efficiency of 13.51%for the flexible OSCs with an area of 0.64 cm2 was achieved based on the PET/barrier film/PVA/AgNWs electrode.The long-term stability showed the flexible OSCs based on the PET/barrier film/PVA/AgNWs electrode have a significantly improved stability relative to the device on PET/AgNWs electrode,and comparable air stability as the rigid device with glass/ITO device.The unencapsulated devices maintained nearly 50%of the original efficiency after storage for 600 h in air.After a simple top encapsulation,the flexible devices remained at 60%of the initial efficiency after 2000 h in the air.Therefore,the flexible AgNWs electrode based on the barrier film would have the potential to improve the air storage stability of organic flexible solar cells.

关 键 词：Flexible organic solar cell AgNWs electrode Air storage stability Barrier films substrate Energy conversion Flexible electronics Interface 