改性纳米防腐色浆的研制  

Development of Modified Nano-Anticorrosive Paste

在线阅读下载全文

作  者:林光宁 林清华 Lin Guangning;Lin Qinghua(Guangdong Power Supply Bureau Co.,Ltd.,Yangjiang Guangdong,529500,China)

机构地区:[1]广东电网有限责任公司阳江供电局,广东阳江529500

出  处:《上海涂料》2024年第2期21-24,共4页Shanghai Coatings

基  金:中国南方电网项目资助:配电变压器重防腐涂层材料及在线修复技术的研究(031700KC23040010)。

摘  要:以丙二醇甲醚为分散介质,通过棒硝式砂磨的工艺制备复合铁钛粉纳米防腐色浆。通过对砂磨后色浆的沉降试验,确定了色浆的最佳的砂磨时间为8 h。通过研究改性剂添加前后对防腐色浆沉降高度、颗粒形貌、粒径分布和zeta电位的影响,最终确定以添加了GL-1110改性剂后所制备的复合铁钛粉纳米防腐色浆最为稳定,其粒径小于10μm,具有较好的分散性。The iron titanium powder anticorrosive paste was prepared by the process of sand milling in propylene glycol methyl ether.The optimum sanding time of the paste was 8 h,which was determined by the sedimentation test.The settling height,particle morphology,particle size distribution and zeta potential of the anticorrosive pastes were compared before and after modification.It was finally determined that the most stable anticorrosive paste system was the one modified with GL-1110.The particle size of the composite iron titanium powder nano-anticorrosive paste prepared was less than 10μm,and it had good dispersibility.

关 键 词:防腐色浆 复合铁钛粉 纳米色浆 改性剂 

分 类 号:TQ630.7[化学工程—精细化工]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象