Evolution of MnO–SiO2–Al_(2)O_(3)–MgO inclusions during heat treatment at 1100℃  

作　　者：Xu-bo Lei Jian-li Li Qiang Zeng Hang-yu Zhu Yue Yu 

机构地区：[1]The State Key Laboratory of Refractories and Metallurgy,Wuhan University of Science and Technology,Wuhan,430081,Hubei,China [2]Hubei Provincial Key Laboratory for New Processes of Ironmaking and Steelmaking,Wuhan University of Science and Technology,Wuhan,430081,Hubei,China [3]Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education,Wuhan University of Science and Technology,Wuhan,430081,Hubei,China

出　　处：《Journal of Iron and Steel Research International》2024年第5期1221-1231,共11页

基　　金：supported by the National Natural Science Foundation of China(Nos.52274341 and 51974210).

摘　　要：To investigate the evolutionary behavior of the MnO–SiO_(2)–Al_(2)O_(3)–MgO inclusions during heat treatment,water quenched samples were isothermally held at 1100°C for 120 min in Ar and air atmosphere,and the obtaining samples were analyzed by X-ray diffraction,scanning electron microscopy and energy dispersive spectrometer.It showed that 3MnO·Al_(2)O_(3)·3SiO_(2)and MnO·SiO_(2)were detected in the 5 wt.%MgO system after isothermal holding in Ar atmosphere,while MgO·Al_(2)O_(3),MnO·SiO_(2)and Mn7O8·SiO4 were detected in air atmosphere.The evolutionary behavior of the 10,15 and 20 wt.%MgO systems after isothermal holding in different atmosphere were consistent.Oxygen affected the solid phase transformation of the low MgO content systems.The calculation results of FactSage 8.1 showed that MgO·Al_(2)O_(3)was formed in the 5 wt.%MgO system with air atmosphere.The solid phase transformation was accompanied by grain coarsening during the isothermal holding process.The differences in the solid phase transformation in different atmosphere of the 5 wt.%MgO system indicated that it was a gas-phase transport grain coarsening mechanism.The enrichment of Al element in the liquid phase region at the grain edges,the homogeneous distribution of Mg element and the disappearance of the liquid phase within the crystal revealed that other MgO content systems were liquid–solid transport grain coarsening mechanism.

关 键 词：EVOLUTION Glassy phase Inclusion Heat treatment MgO·Al_(2)O_(3) 

分 类 号：TF046[冶金工程—冶金物理化学]