桑蚕的强制牵伸抽丝及其纤维性能  

Properties of Bombyx mori silkworm silk obtained by forced reeling

作　　者：刘术 侯腾[1] 周乐乐 李祥龙[1] 杨斌[1] LIU Shu;HOU Teng;ZHOU Lele;LI Xianglong;YANG Bin(College of Textile Science and Engineering(International Institute of Silk),Zhejiang Sci-Tech University,Hangzhou,Zhejiang 310018,China)

机构地区：[1]浙江理工大学纺织科学与工程学院(国际丝绸学院),浙江杭州310018

出　　处：《纺织学报》2024年第6期11-15,共5页Journal of Textile Research

基　　金：浙江省自然科学基金项目(Y21E030049)。

摘　　要：为提升蚕丝的力学性能,采用一种圆锥斜面牵伸装置对五龄桑蚕进行强制牵伸抽丝以制备高强牵伸丝,研究不同牵伸速度对桑蚕牵伸丝形貌、力学性能的影响,并将牵伸丝与蚕丝进行对比与分析。结果表明:由强制抽丝获得的牵伸丝表面光滑平坦,丝胶均匀附着;随着牵伸速度的增加,牵伸丝截面逐渐向弓形转变;牵伸丝的综合力学性能显著优于蚕丝,且其断裂强度、弹性模量、断裂比功与断裂伸长率随着牵伸速度的增加均有不同程度的增加;其中,以接近桑蚕自然吐丝速度(1 cm/s)牵伸制备的牵伸丝的断裂强度与蚕丝相当,约为3.00 cN/dtex,但其弹性模量(93.10 cN/dtex)远高于蚕丝(76.90 cN/dtex);当牵伸速度增加至4 cm/s时,可获得力学性能最佳的牵伸丝,其断裂伸长率为22.49%,断裂强度为3.39 cN/dtex,弹性模量为95.76 cN/dtex,断裂比功为0.62 cN/dtex,相比于蚕丝的平均值分别提高了7%、13.76%、24.53%、31.91%。Objective Bombyx mori silk fibers have an interesting and elaborate structure,but its mechanical properties are inferior to spider dragline silk.Therefore,it is of great significance to prepare Bombyx mori silk comparable to spider silk.Traditional silk processing technology,however,is difficult to enhance the performance of cocoon silk,and even damage its morphology and properties.In addition,artificial silk produced by a variety of spinning methods cannot fully replicate the properties of natural silk.Herein,we proposed a simple and effective strategy for preparing high-strength Bombyx mori silk,which not only retains the hierarchical structure of natural silk,but also advances its mechanical properties.Method Inspired by spider silking,this work designed a conical forced reeling device that can consistently reel silk from the fifth instar silkworm at controlled reeling speed.In this study,the silkworms were forcibly reeled at 1-4 cm/s,resulting in the force-reeled silk fibers(FRSF-1,FRSF-2,FRSF-3,and FRSF-4).During forced reeling,the silk was fully stretched due to a recombination of the reeling force and the gravity of silkworm,which increased the orientation and crystallinity of FRSFs.Meanwhile,the cocoon silk fibers(CSFs)selected from the same batch were set as a control group.In addition,the characteristic of fiber morphology,fineness,and mechanical properties of all silk samples were performed.Results The FRSFs have a smooth and uniform morphology,and a bow-shaped cross-section,which differs significantly from that of CSFs.Specifically,the transversal surface of FRSF-1 is almost a round triangular cross-section shaped like CSFs,and both the rounded triangular and bow-shaped cross-section appeared in FRSF-2.With the reeling speed further increasing,only bow-shaped transverse section can be found in FRSF-3 and FRSF-4.Furthermore,the mechanical properties including breaking elongation,stress,elastic modulus,and specific work of rupture of FRSFs are superior to that of CSFs.First of all,the stress of FRSFs in

关 键 词：桑蚕 蚕丝 强制抽丝 牵伸丝 力学性能 

分 类 号：TS102.3[轻工技术与工程—纺织工程] TS143.2[轻工技术与工程—纺织科学与工程]