低红外发射率控温热红外伪装材料的制备与性能  

Preparation and properties of low infrared emissivity temperature-controlled thermal infrared camouflage materials

作　　者：时吉磊 陈廷彬 付少海 张丽平[1,2] SHI Jilei;CHEN Tingbin;FU Shaohai;ZHANG Liping(Jiangsu Engineering Research Center for Digital Textile Inkjet Printing,Wuxi,Jiangsu 214122,China;Key Laboratory of Eco-Textiles(Jiangnan University),Ministry of Education,Wuxi,Jiangsu 214122,China)

机构地区：[1]江苏省纺织品数字喷墨印花工程技术研究中心,江苏无锡214122 [2]生态纺织教育部重点实验室(江南大学),江苏无锡214122

出　　处：《纺织学报》2024年第6期32-38,共7页Journal of Textile Research

基　　金：江苏省自然科学基金项目(BK20211240);江南大学大学生创新创业训练项目(202410295195Y)。

摘　　要：目前,仅从阻隔目标热量散发或降低表面红外发射率单方面入手很难达到理想的热红外伪装效果。针对这一问题,通过在聚丙烯腈静电纺丝液中混合相变材料聚乙二醇和性价比较高的铁纳米粒子,采用静电纺丝技术制备了一种外表面具有低红外发射率、底层具有控温功能的复合纤维膜材料,分析了复合纤维膜的表观形貌、化学及物相结构、热学性能、红外发射率和控温性能,研究了复合材料的红外隐身性能。结果表明:当聚乙二醇4000和聚乙二醇1000投料比不同时,可得到相变温度在31.5~40.9℃之间的系列相变纤维膜;复合纤维膜的红外发射率最低为0.69,在55℃热台上能够产生12℃的表面温度差,最大可产生22.4℃的辐射温度差,与环境温度相比最低具有1.9℃的辐射温度差,使目标在红外热成像中与环境辐射颜色一致。Objective Infrared(IR)stealth is essential in modern military.With the rapid development of infrared detection technology,effectively hiding targets and rendering them invisible to thermal infrared detectors have been great challenges.Infrared stealth effect is affected by both temperature and infrared emissivity,but most of the previous studies focused on a single factor,which limits the effectiveness of the products.In order to achieve better infrared stealth effect,a composite fiber membrane material was prepared with low infrared emissivity on the outer surface and temperature control function inside.Method The continuous electrospinning method was used to prepare the composite fiber membrane with the effect of controlling temperature and moderating infrared emissivity.By controlling the mass ratio of polyethylene glycol(PEG1000 and PEG4000)and the amount of nano-iron particles,the fiber membrane with different phase change temperature and infrared emissivity was obtained.The mass ratio between PEG4000 and PEG1000 was 2∶1,3∶2,1∶1 and 2∶3,and nano-iron particles accounted for 10%,20%,and 30%of the PAN quality,respectively.The apparent morphology,chemical and phase structure,thermal properties and infrared emissivity of the composite fiber membranes were studied.The infrared stealth properties of composites were investigated.Results The surface of pure PAN fibers is smooth and the diameter distribution is uniform.The phase change fibers doped with polyethylene glycol became rough and wrinkled,and some fibers exhibited a fine groove-like morphology,which is,however,regular without showing polymer intorface separation.The composite fiber was well formed and showed certain dimensional stability.The infrared spectrum demonstrated that PAN(polyacrylonitrile)and PEG(Polyethylene glycol)have good binding and compatibility,which is consistent with the results of SEM.With the different mass ratios of PEG4000 and PEG1000,the phase transition temperature was between 31.5-40℃,with a regulation range of about 10�

关 键 词：聚丙烯腈 聚乙二醇 铁纳米粒子 红外隐身 静电纺丝 复合纤维膜 相变温度 红外发射率 

分 类 号：TS101.8[轻工技术与工程—纺织工程]