Fabrication of Core-Shell Hydrogel Bead Based on Sodium Alginate and Chitosan for Methylene Blue Adsorption  

作　　者：Xiaoyu Chen 

机构地区：[1]School of Material Engineering,Jinling Institute of Technology,Nanjing,211169,China

出　　处：《Journal of Renewable Materials》2024年第4期815-826,共12页可再生材料杂志（英文）

摘　　要：A novel core-shell hydrogel bead was fabricated for effective removal of methylene blue dye from aqueous solutions.The core,made of sodium alginate-g-polyacrylamide and attapulgite nanofibers,was cross-linked by Calcium ions(Ca^(2+)).The shell,composed of a chitosan/activated carbon mixture,was then coated onto the core.Fourier transform infrared spectroscopy confirmed the grafting polymerization of acrylamide onto sodium alginate.Scanning electron microscopy images showed the core-shell structure.The core exhibited a high water uptake ratio,facilitating the diffusion of methylene blue into the core.During the diffusion process,the methylene blue was first adsorbed by the shell and then further adsorbed by the core.Adsorption tests showed that the coreshell structure had a larger adsorption capacity than the core alone.The shell effectively enhanced the adsorption capacity to methylene blue compared to the single core.Methylene blue was adsorbed by activated carbon and chitosan in the shell,and the residual methylene blue diffused into the core and was further adsorbed.

关 键 词：Core-shell structure hydrogel bead attapulgite nanofiber sodium alginate POLYACRYLAMIDE methylene blue adsorption material 

分 类 号：O62[理学—有机化学]