生铁遗传性对球墨铸铁性能的影响  

Influence of Pig Iron Inheritance on the Properties of Nodular Cast Iron

作　　者：李晓艳 赵培根 马宏军 杨麟 俞健良 LI Xiao-yan;ZHAO Pei-gen;MA Hong-jun;YANG Lin;YU Jian-liang(Ningbo Riyue Heauy Industry Joint Stock Company,Ningbo Zhejiang 315113,China;Ningbo Mingling Technology Co.,Itd.,Ningbo Zhejiang 315700,China;Ningbo Rixing Casting Co.,Ltd.,Ningbo Zhejiang 315700,China)

机构地区：[1]宁波日月重工股份有限公司,浙江宁波315113 [2]宁波明凌科技有限公司,浙江宁波315700 [3]宁波日星铸业有限公司,浙江宁波315700

出　　处：《铸造设备与工艺》2024年第3期79-84,共6页Foundry Equipment & Technology

摘　　要：研究了同样的炉料配比情况下,生铁种类对球磨铸铁性能的影响。试验浇注温度为1340℃~1350℃,浇注边长250 mm的立方块,观察其显微组织,并进行性能测试。结果表明:相同生产条件下,不同生铁在占比相同的情况下,其自身组织形态对球墨铸铁的石墨大小、球化率、组织及性能有明显的差异,其中石墨球数量与低温冲击性能的影响程度最大,A、B、C、D生铁的边缘与心部每平方毫米石墨跨度分别在10~25与20~35两区间。The effects of pig iron types on the properties of ductile iron with the same charge ratio were studied.The cube with side length of 250 mm was poured at 1340℃~1350℃,and its microstructure was observed and its performance was tested.The results showed that under the same production conditions,the self-organization morphology of different pig irons had significant differences in the graphite size,spheroidization rate,structure and properties of nodular cast iron under the same proportion,among which the number of graphite balls had the greatest impact on the low-temperature impact performance.The edges and hearts of pig iron A,B,C,and D have graphite spans of 10~25 and 20~35 per square millimeter,respectively.

关 键 词：球墨铸铁 生铁种类 显微组织 组织形态 石墨大小 球化率 

分 类 号：TG255[金属学及工艺—铸造]