高强度合金钢应力腐蚀性能研究  

Study on Stress Corrosion Behavior of High Strength Alloy Steel

作　　者：董志翔 杨俊峰 范芳雄 王灵水 DONG Zhixiang;YANG Junfeng;FAN Fangxiong;WANG Lingshui(CSSC Shuangrui(Luoyang)Special Equipment Co.,Ltd.,Luoyang 471000,China)

机构地区：[1]中船双瑞(洛阳)特种装备股份有限公司,河南洛阳471000

出　　处：《材料开发与应用》2024年第3期56-60,共5页Development and Application of Materials

摘　　要：通过真空熔炼法制备高强度合金钢,采用慢应变速率拉伸测试法检测应力腐蚀敏感性。结果表明,随着材料强度的增加,应力腐蚀敏感性变大,断口出现沿晶形貌,属于脆性断裂;不同材料进行充氢试验后,慢拉伸试样的H残留量随着Mo含量的增加而增加,说明Mo含量对H残留有一定的影响。High strength alloy steel is prepared by vacuum melting method,and the stress corrosion sensitivity is tested by slow strain rate tensile test.The results show that with the increase of material strength,the stress corrosion susceptibility becomes larger,and the fracture surface shows intergranular morphology,which belongs to brittle fracture.After the hydrogen charging test of different materials,the residual amount of H in slow tensile specimens increases with the increase of Mo content,which shows that Mo content has a certain effect on the residual amount of H.

关 键 词：高强度合金钢 氢 应力腐蚀开裂 

分 类 号：TG156.9[金属学及工艺—热处理]