氰酸酯树脂改性环氧树脂的冲击强度及介电性能  

Impact strength and dielectric properties of epoxy resin modified by cyanate ester

作　　者：贺星 刘星辰 袁剑伟 杜瑞奎[1,2] 陈启辉 刘亚青 赵贵哲[1,2] HE Xing;LIU Xingchen;YUAN Jianwei;DU Ruikui;CHEN Qihui;LIU Yaqing;ZHAO Guizhe(School of Materials Science and Engineering,North University of China,Taiyuan 030051,China;Research Center for Engineering Technology of Polymeric Composites of Shanxi Province,Taiyuan 030051,China)

机构地区：[1]中北大学材料科学与工程学院,太原030051 [2]山西省高分子复合材料工程技术研究中心,太原030051

出　　处：《工程塑料应用》2024年第7期139-147,共9页Engineering Plastics Application

摘　　要：为降低制备成本,采用低含量氰酸酯(CE)增韧改性环氧(EP)树脂,制备了EP/CE共聚物。利用差示扫描量热分析仪和傅里叶变换红外光谱仪分析了EP/CE的固化过程,研究了CE用量对EP/CE冲击强度的影响,并进一步分析了EP/CE的弯曲性能、介电性能和热性能。结果表明,CE改性EP树脂的冲击强度显著提高,当CE添加质量为EP树脂的0.2时,改性效果最好,冲击强度从3.46 kJ/m^(2)增加到5.81 kJ/m^(2),同时,弯曲模量从2.71 GPa增加到3.47 GPa;常温下2~18 GHz频率范围内的介电损耗角正切值降低到0.0298附近;而玻璃化转变温度和初始分解温度稍有降低,分别为117.0℃和328.9℃。EP/CE共聚物良好的力学、介电和热性能可以拓宽EP树脂基复合材料在大批量生产工业领域的应用范围。To reduce preparation costs,low content of cyanate ester(CE)was used to enhance the toughness of the epoxy(EP)resin.EP/CE copolymer was prepared and the curing process was studied by differential scanning calorimeter and Fourier infrared spectrometer.The influence of CE on the impact strength of EP/CE copolymer was studied,as well as the flexural properties,dielectric properties and thermal properties.The results show that the EP/CE copolymer exhibits the best impact strength when the addition of CE is 0.2 of epoxy resin,and the impact strength of the modified EP resin significantly increases from 3.46 kJ/m^(2) to 5.81 kJ/m^(2).In addition,the flexural modulus also significantly improves from 2.71 GPa to 3.47 GPa,and the dielectric loss angle tangent of 2~18 GHz frequency range at room temperature decreases to 0.0298.The glass transition temperature and initial decomposition temperature decrease to 117.0℃and 328.9℃,respectively.The EP/CE copolymer with good mechanical,dielectric and thermal properties can broaden the application of EP resin composites in mass production.

关 键 词：环氧树脂 氰酸酯树脂 冲击强度 弯曲模量 介电性能 

分 类 号：TQ322[化学工程—合成树脂塑料工业]