研究堆用铝合金辐照性能研究  

Study of Irradiation Properties of Aluminum Alloy in Research Reactor

作　　者：曾珍 杨笑[2] 房永刚 蔡光博 初起宝 张宇[2] 汤琪[2] 张长义[2] 马若群 ZENG Zhen;YANG Xiao;FANG Yonggang;CAI Guangbo;CHU Qibao;ZHANG Yu;TANG Qi;ZHANG Changyi;MA Ruoqun(Nuclear and Radiation Safety Center,Ministry of Ecology and Environment,Beijing 102400,China;China Institute of Atomic Energy,Beijing 102413,China)

机构地区：[1]生态环境部核与辐射安全中心,北京102400 [2]中国原子能科学研究院,北京102413

出　　处：《原子能科学技术》2024年第8期1621-1627,共7页Atomic Energy Science and Technology

基　　金：国家重点研发计划(2019YFB1900900)。

摘　　要：铝合金由于其较好的力学性能和优良的抗中子辐照性能,常被选作研究堆关键部位的结构材料。随着研究堆运行寿命的增加,该结构材料经过高中子注量的辐照后,其力学性能是否能满足堆芯结构完整性要求值得关注,本文基于上述问题对铝合金的辐照性能开展研究,获取了研究堆辐照孔道及堆芯支撑结构材料(LT-21型铝合金)拉伸试验及冲击试验数据。Owing to its intrinsic superior characteristics of good conductivity,light weight,high specific strength,easy processing,small thermal neutron cross sections,small activation cross sections,fast decay of radiation induced radiation energy,good corrosion resistance and radiation resistance,aluminum alloy are commonly used as core structure support materials,component cladding materials,container pipeline materials,etc.As core structure support materials in research reactors with much bad service environment,aluminum alloy must endure a large amount of radiation and high-energy particle bombardment,which will result in macroscopic changes in support material’s mechanical properties.So far,few relative research can be found on the irradiation performance of aluminum alloy structural materials both domestically and internationally,due to the fact that the irradiation effect is related to the crystal type,microstructure,and service environment,such as irradiation dose,temperature,etc.Therefore,it is of great significance to study the radiation damage mechanism of aluminum alloy and the changes in their mechanical properties after irradiation.Radiation damage includes fast neutron irradiation damage and thermal neutron irradiation damage.Thermal neutron irradiation damage causes changes in the chemical composition of structural materials through transmutation.The silicon content of aluminum alloy increases after irradiation transmutation,and relative research shows that an increase in silicon content could improve structural material’s ductility and formability.Fast neutron irradiation damage changes the internal structure of crystals through high-energy particles,resulting in defects such as dislocation loops and stacking faults,resulting in the changes of the mechanical properties of material.Irradiation experiments and mechanical tests were conducted to investigate the mechanisms of radiation damage of aluminum alloy.Based on present experiments and tests data,irradiation performance of aluminum alloys and the m

关 键 词：研究堆 铝合金 辐照性能 冲击试验 

分 类 号：TL341[核科学技术—核技术及应用]