丙烯酸酯阻尼乳液聚合水性车用涂料制备及粘附性能研究  

Study on preparation and bonding properties of water-based polymerized coatings with acrylic damping emulsion for rail vehicles

作　　者：邢宏楠 XING Hongnan(CRRC Changchun Rail Transit Co.,Ltd.,Changchun 130062,China)

机构地区：[1]中车长春轨道客车股份有限公司,吉林长春130062

出　　处：《粘接》2024年第8期13-16,共4页Adhesion

摘　　要：为了缓解轨道交通工具中的噪声问题,丙烯酸酯阻尼乳液是一种高效的阻尼材料,利用乳液聚合法制备丙烯酸酯阻尼乳液,以甲基丙烯酸羟乙酯(HEMA)为功能性单体,实现核壳改性丙烯酸酯阻尼乳液,在该改性乳液基础上添加甲醛次硫酸氢钠等材料,制备出轨道车辆用丙烯酸酯阻尼乳液聚合水性涂料。试验结果显示,该涂料对于活性较强的冷轧钢、铝型材料等粘附剥离强度较高,但不适合粘附非金属材料;当HEMA用量加大时,该涂料的初粘性与持粘性的性能较好。综合考虑,HEMA添加要适量。In order to alleviate the noise problem in rail transit,acrylate damping emulsion is a kind of efficient damping material,the acrylate damping emulsion was prepared by emulsion polymerization method,hydroxyethyl methacrylate(HEMA)was used as a functional monomer to realize the core-shell modified acrylate damping emul⁃sion,and formaldehyde sodium bisulfite and other materials were added on the basis of the modified emulsion to pre⁃pare acrylate damping emulsion polymerization water-based coatings for rail vehicles.The test results showed that the coating had high adhesive stripping strength for active cold rolled steel and aluminum profiles,but was not suit⁃able for bonding non-metallic materials.When the amount of HEMA increased,the initial viscosity and viscosity performance of the coating were better.It needs to be considered comprehensively to select the amount of HEMA.

关 键 词：轨道车辆 丙烯酸酯 阻尼乳液 涂料制备 粘附性能 

分 类 号：TQ630.7[化学工程—精细化工]