Magnetic properties and magnetocaloric effects in Eu(Ti,Nb,Mn)O_(3) perovskites  

作　　者：Junfeng Wang Huicai Xie Quanyi Liu Zhihong Hao Zhaojun Mo Qi Fu Xinqiang Gao Jun Shen 

机构地区：[1]Ganjiang Innovation Academy,Chinese Academy of Sciences,Ganzhou,341119,China [2]Faculty of Materials Metallurgy and Chemistry,Jiangxi University of Science and Technology,Ganzhou,341000,China [3]School of Rare Earth and New Materials Engineering,Gannan University of Science and Technology,Ganzhou,341000,China [4]Department of Energy and Power Engineering,School of Mechanical Engineering,Beijing Institute of Technology,Beijing,100081,China

出　　处：《Journal of Rare Earths》2024年第8期1560-1567,I0006,共9页稀土学报（英文版）

基　　金：Research Projects of Ganjiang Innovation Academy,Chinese Academy of Sciences (No.E055B002) for providing financial support。

摘　　要：In perovskite EuTiO_(3),the magnetic characteristics and magnetocaloric effect(MCE) can be flexibly regulated by converting the magnetism from antiferromagnetic to ferromagnetic.In the present work,a series of Eu(Ti,Nb,Mn)O_(3) compounds,abbreviated as ETNMO for convenience of description,was fabricated and their crystallography,magnetism together with cryogenic magnetocaloric effects were systematically investigated.The crystallographic results demonstrate the cubic perovskite structure for all the compounds,with the space group of Pm3m.Two magnetic phase transitions are observed in these second-order phase transition(SOPT) materials.The joint substitution of elements Mn and Nb can considerably manipulate the magnetic phase transition process and magnetocaloric performance of the ETNMO compounds.As the Mn content increases,gradually widened-ΔS_(M)-T curves are obtained,and two peaks with a broad shoulder are observed in the-ΔS_(M)-T curves for Δμ_(0)H≤0-1 T.Under a field change of 0-5 T,the values of maximum magnetic entropy change(-ΔS_(M)^(max)) and refrigeration capacity(RC) are evaluated to be 34.7 J/(kg·K) and 364.9 J/kg for EuTi_(0.8625)Nb_(0.0625)Mn_(0.075)O_(3), 27.8 J/(kg·K) and367.6 J/kg for EuTi_(0.8375)Nb_(0.0625)Mn_(0.1)O_(3),23.2 J/(kg·K) and 369.2 J/kg for EuTi_(0.8125)Nb_(0.0625)Mn_(0.125)O_(3),17.1 J/(kg·K) and 357.6 J/kg for EuTi_(0.7875)Nb_(0.0625)Mn_(0.15)O_(3),respectively.The co nsiderable MCE parameters make the ETNMO compounds potential candidates for cryogenic magnetic refrigeration.

关 键 词：ETNMO perovskites Cryogenic refrigeration Magnetic phase transition Magnetocaloric effect Rare earths 

分 类 号：TB64[一般工业技术—制冷工程]