焊趾熔修和超声冲击处理对船用钢焊接接头的影响  

Influence of Weld Toe Repair and Ultrasonic Impact Treatment on the Welded Joints of Marine Steel

在线阅读下载全文

作  者:何亮 贺智涛 张蕾 程彬 马晓阳 丁鹏龙 HE Liang;HE Zhitao;ZHANG Lei;CHENG Bin;MA Xiaoyang;DING Penglong(Luoyang Ship Material research Institute,Luoyang 471023,China)

机构地区:[1]中国船舶集团有限公司第七二五研究所,河南洛阳471023

出  处:《电焊机》2024年第8期96-101,共6页Electric Welding Machine

摘  要:针对船用钢焊接接头性能薄弱易发生疲劳断裂的问题,分别采用超声冲击、焊趾熔修和焊趾熔修+超声冲击复合处理等三种方法对船用高强钢焊接接头进行强化,对不同工艺强化后接头的残余应力、应力集中系数和疲劳性能进行了对比试验研究。结果表明:(1)超声冲击处理可有效降低接头残余应力,在表面形成有益的压应力,而焊趾熔修对接头残余应力无改善作用,甚至会使残余应力略增大;(2)三种处理工艺均可降低焊趾处应力集中程度,焊趾熔修处理可显著降低焊趾应力集中系数;(3)三种处理工艺均可改善接头低周疲劳性能,超声冲击处理后接头疲劳寿命提高幅度为58%,焊趾熔修处理后疲劳寿命提高幅度为249%,焊趾熔修+超声冲击复合处理后疲劳寿命提高幅度为460%。焊趾熔修+超声冲击复合处理工艺兼顾了焊趾熔修处理和超声冲击处理的优点,既可显著降低焊趾应力集中程度又可获得有益的残余压应力,可应用于船舶焊接结构关键部位的强化。Aiming at the problem of weak performance and easy fatigue fracture of welded joints of Marine steel,three methods were used to strengthen the welded joint of marine high-strength steel,including ultrasonic impact,weld toe repair and weld toe repair+ultrasonic impact composite treatment.The residual stress,stress concentration factor and fatigue performance of the joint strengthened by different processes were compared and studied.The results show that:(1)ultrasonic impact treatment can effectively reduce the residual stress of the joint and form beneficial compressive stress on the surface,while weld toe repair can not improve the residual stress of the joint,and even slightly increase the residual stress;(2)All three treatment processes can reduce the stress concentration at the weld toe,and the weld toe repair treatment can significantly reduce the stress concentration coefficient;(3)All the three treatment processes can improve the low-cycle fatigue performance of the joint.The fatigue life of the joint is increased by 58%after ultrasonic impact treatment,by 249%after weld toe repair,and by 460%after weld toe repair combined with ultrasonic impact treatment.The compound treatment process of weld toe repair and ultrasonic impact gives consideration to the advantages of weld toe repair and ultrasonic impact treatment,which can not only significantly reduce the stress concentration of weld toe,but also obtain beneficial residual compressive stress,and can be applied to strengthening key parts of ship welded structure.

关 键 词:超声冲击 焊趾熔修 残余应力 疲劳性能 焊接接头 

分 类 号:TG111.5[金属学及工艺—物理冶金]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象