滚压量对300M钢螺栓退刀槽表面完整性的影响  

Influence of Rolling Amount on the Surface Integrity of 300M Steel Bolt Backing Groove

作　　者：岳美茹 郭晓光[1] 康仁科[1] 朱祥龙 刘宏伟[1] 王梓悦 YUE Meiru;GUO Xiaoguang;KANG Renke;ZHU Xianglong;LIU Hongwei;WANG Ziyue(School of Mechanical Engineering,Dalian University of Technology,Dalian 116024,China)

机构地区：[1]大连理工大学机械工程学院,大连116024

出　　处：《中国表面工程》2024年第3期195-203,共9页China Surface Engineering

基　　金：国家商用飞机制造工程技术研究中心创新基金(COMAC-SFGS-2022-1814)。

摘　　要：滚压加工是螺栓表面强化的主要方法,但关于滚压参数对高强度钢螺栓表面质量的影响规律研究鲜有报道。为了研究滚压量对300M钢螺栓退刀槽表面完整性的影响,使用zygo表面粗糙度轮廓仪、超景深显微镜、显微硬度计、X射线应力衍射仪、扫描电镜等设备,对滚压后螺栓退刀槽表面粗糙度、表面形貌、显微硬度、残余应力、表层显微组织等进行检测。结果表明:随着滚压量的增大,表面粗糙度先减小后增大,当滚压量为0.08 mm时,表面粗糙度Sa达到最小值0.058μm,相比滚压前减小75%;螺栓退刀槽表层晶粒明显细化,并形成高密度位错,滚压量为0.11 mm时塑性变形层深最大达166μm;塑性变形使螺栓表层显微硬度显著增加,最大值为660 HV,相比基体硬度提高16%,形成280~400μm的硬化层;滚压加工给螺栓表面引入较大的残余压应力,且随滚压量增加逐渐增大,残余压应力最大达848.4MPa。研究结果补充了300M高强钢螺栓退刀槽滚压表面完整性数据,可应用于工艺人员对民机、军机等螺栓断裂原因分析、疲劳寿命预测及螺栓滚压加工参数优选。Because of their high strength,precision,and hardness,300M steel bolts are widely used in the assembly of various aircraft structural parts.Owing to long-term service in extreme environments,such as severe vibrations and large temperature differences,fatigue damage is prone to occur at the bolt-backing groove,resulting in major safety accidents.Rolling processing,which has dual functions of surface finishing and surface strengthening,is the primary processing technology for bolt surface strengthening.The selection of rolling parameters has significant influence on surface integrity and fatigue life.The rolling amount is an important parameter in the rolling process.To effectively improve the surface quality and performance of the bolt,a rolling strengthening test of the bolt-back groove under different rolling amounts was conducted on a self-developed special rolling tooling for bolts.The effect of the rolling amount on the surface integrity of the 300 M steel bolts was studied.Based on the previous test,the rolling amounts were selected as 0.05 mm,0.08 mm,and 0.11 mm,respectively.The surface roughness,surface morphology,microhardness,residual stress,and surface microstructure of a 300 M steel bolt after back-groove rolling were tested using a Zygo surface roughness tester,super depth-of-field microscope,microhardness tester,X-ray stress diffractometer,and scanning electron microscope.The results showed that with an increase in the rolling amount,the surface roughness initially decreases and then increases.When the rolling amount is 0.08 mm,the surface roughness Sa reaches the minimum value of 0.058μm,which is 75%lower than that before rolling.The surface morphology of the bolt reaches the optimal state when the rolling amount is 0.08 mm,the turning marks basically disappear,and the surface is the most polished.As the rolling amount increases,the surface quality is destroyed,and a large number of pits and ploughs appear.The rolling process causes plastic deformation of the bolt surface structure,and the martensi

关 键 词：300M钢螺栓 滚压量 表面粗糙度 微观组织 表层硬度 残余应力 

分 类 号：TG668[金属学及工艺—金属切削加工及机床]