腈基改性醚化酚醛树脂的制备与性能研究  

Study on the Preparation and Properties of Nitrile-based Modified Etherified Phenolic Resin

作　　者：杨娜[1] 张大勇[1] 刘晓辉[1] 王刚[1] 李欣[1] 赵颖[1] 朱金华[1] YANG Na;ZHANG Dayong;LIU Xiaohui;WANG Gang;LI Xin;ZHAO Ying;ZHU Jinhua(Institute of Petrochemistry,Heilongjiang Academy of Sciences,Harbin 150040,China)

机构地区：[1]黑龙江省科学院石油化学研究院,黑龙江哈尔滨150040

出　　处：《化学与粘合》2024年第5期453-456,503,共5页Chemistry and Adhesion

摘　　要：通过4-硝基邻苯二甲腈与醚化酚醛树脂间的亲核取代反应,制备了邻苯二甲腈改性醚化酚醛树脂。采用FT-IR、DSC、TGA和万能拉力试验机对其结构和力学性能进行了研究。结果表明,不同腈基改性比例的树脂热性能均有提升。在氮气气氛下,CN-BPF-1的800℃残炭率达到了69%,比醚化酚醛提高了20%,表现出高残炭的特点;其2%失重温度、5%失重温度分别为348.7℃、386.0℃,比醚化酚醛树脂分别提高了66.2℃、9.9℃;力学性能得到明显提升,其中CN-BPF-1的室温、250℃和350℃剪切强度比醚化酚醛分别提高了9.3MPa、9.8MPa和6.8 MPa。The phthalonitrile modified etherified phenolic resin is prepared by nucleophilic substitution reaction between 4-nitrophthalonitrile and etherified phenolic resin.The structural and mechanical properties are investigated by FT-IR,DSC,TGA and universal tensile testing machine.The results show that the thermal properties of the resin are enhanced with different modification ratios.Under nitrogen atmosphere,the char yield of CN-BPF-1 reaches 69% at 800 ℃,which is 20% higher than that of etherified phenolic resin,showing a characteristic of high carbon yield;its 2%weight loss temperature and 5% weight loss temperature is 348.7 ℃ and 386.0 ℃ respectively,which is 66.2 ℃ and 9.9 ℃ higher than that of etherified phenolic resin;The mechanical properties are significantly improved,among which the shear strengths of CN-BPF-1 at room temperature,250℃ and 350℃ increases by 9.3 MPa,9.8 MPa and 6.8 MPa respectively,compared with that of etherified phenolic resin.

关 键 词：邻苯二甲腈 醚化酚醛树脂 耐热改性 

分 类 号：TQ323.1[化学工程—合成树脂塑料工业]