单壁碳纳米管/聚醚酰亚胺电磁屏蔽薄膜的制备与性能  

Preparation and properties of single-walled carbon nanotube/polyetherimide electromagnetic shielding film

作　　者：王天赐 夏乾善 黄信佐 王永正 刘斌 张晋通 黎涛 Wang Tian-Ci;Xia Qian-Shan;Huang Xin-Zuo;Wang Yong-Zheng;Liu Bin;Zhang Jin-Tong;Li Tao(Key Laboratory of Engineering Dielectric and Applications(Ministry of Education),School of Electrical and Electronic Engineering,Harbin University of Science and Technology,Harbin 150080,China;AVIC Research Institute for Special Structures of Aeronautical Composites,Ji’nan 250023,China)

机构地区：[1]哈尔滨理工大学电气与电子工程学院,工程电介质及其应用教育部重点实验室,哈尔滨150080 [2]中国航空工业集团公司济南特种结构研究所,济南250023

出　　处：《物理学报》2024年第17期277-284,共8页Acta Physica Sinica

基　　金：中国博士后科学基金(批准号:2021M701019);黑龙江省博士后资助项目(批准号:LBH-Z20069);黑龙江省高校基础研究基金(批准号:2022-KYYWF-0152)资助的课题.

摘　　要：在实际应用中,柔性、轻质、高性能是聚合物基电磁屏蔽材料应具备的特点.目前,制备兼具优异电导率、电磁屏蔽性能和力学性能的聚合物基电磁屏蔽材料仍然是一个巨大挑战.因此,本工作以单壁碳纳米管和聚醚酰亚胺为原料,通过静电纺丝和真空辅助过滤的方法制备了单壁碳纳米管/聚醚酰亚胺复合薄膜.通过调控单壁碳纳米管的面密度,复合薄膜的电导率可以提升至1866 S/cm.对于电磁屏蔽性能,单壁碳纳米管/聚醚酰亚胺复合薄膜在Ku波段(12-18 GHz)的总电磁屏蔽效能为75.78-81.83 dB,高于纯单壁碳纳米管薄膜的电磁屏蔽效能(65.19-69.81 dB).由于聚醚酰亚胺纤维和单壁碳纳米管之间形成了界面,在一定的单壁碳纳米管面密度范围内,界面越多,消耗的电磁波能量越多.对于力学性能,单壁碳纳米管/聚醚酰亚胺薄膜的最大拉伸强度和断裂伸长率分别为28.52 MPa和7.91%,是单壁碳纳米管薄膜的1.13倍和1.5倍,随着单壁碳纳米管面密度的增大,单壁碳纳米管之间的相互作用以及聚醚酰亚胺纤维和单壁碳纳米管在界面处的相互作用对复合薄膜的力学性能起到了一定的增强作用.单壁碳纳米管/聚醚酰亚胺复合薄膜作为一种优异的聚合物基电磁屏蔽复合材料,可用于如精密电子仪器的防护和可穿戴电子设备等领域.In practical applications,flexibility,lightweight,and high performance are the characteristics that polymerbased electromagnetic shielding materials should have.At present,it is still a great challenge to prepare polymer-based electromagnetic shielding materials with excellent conductivity,electromagnetic shielding properties,and mechanical properties.Therefore,in this work,single-walled carbon nanotubes/polyetherimide composite films are prepared by electrostatic spinning and vacuum-assisted filtration through using singlewalled carbon nanotubes and polyetherimide as raw materials.By regulating the surface density of single-walled carbon nanotubes,the conductivity of the composite film can be enhanced to 1866 S/cm.For the electromagnetic shielding performance,the total electromagnetic shielding effectiveness of single-walled carbon nanotubes/polyetherimide composite film in Ku band(12–18 GHz)is in a range of 75.78–81.83 dB,which is higher than that of pure single-walled carbon nanotube film(65.19–69.81 dB).This is attributed to the formation of interfaces between the polyetherimide fibers and the single-walled carbon nanotubes,with more interfaces consuming more electromagnetic wave energy for a given range of single-walled carbon nanotube surface densities.For the mechanical properties,the maximum tensile strength and elongation at the break of the single-walled carbon nanotube/polyetherimide film are 1.13 and 1.5 times higher than those of the singlewalled carbon nanotube film,with the values of 28.52 MPa and 7.91%,respectively.As the surface density of single-walled carbon nanotubes increases,the interaction between single-walled carbon nanotubes as well as the interaction between polyetherimide fibers and single-walled carbon nanotubes at the interface plays a role in enhancing the mechanical properties of the composite films.The single-walled carbon nanotube/polyetherimide composite films,as an excellent polymer-based electromagnetic shielding composite material,can be used in fields such as the prote

关 键 词：单壁碳纳米管 聚醚酰亚胺 静电纺丝 电磁屏蔽 

分 类 号：TB383.2[一般工业技术—材料科学与工程]