氧化物负载磷钨酸催化甘露醇脱水反应的研究  

Dehydration of Mannitol Catalyzed by Oxide Supported Phosphotungstic Acid

作　　者：陈涵铭 莫学坤 郑燕春 徐冰冰 侯铭轩 葛峻逍 朱明乔[1,2] CHEN Hanming;MO Xuekun;ZHENG Yanchun;XU Bingbing;HOU Mingxuan;GE Junxiao;ZHU Mingqiao(College of Chemical and Biological Engineering,Zhejiang University,Hangzhou 310058,China;Institute of Zhejiang University-Quzhou,Quzhou 324000,China;Zhejiang Zhenghe Fluid Technology Company Limited,Hangzhou 310014,China;Quzhou Juhua Polyamide Fibre LLC,Quzhou 324000,China)

机构地区：[1]浙江大学化学工程与生物工程学院,浙江杭州310058 [2]浙江大学衢州研究院,浙江衢州324000 [3]浙江江正和流体科技股份有限公司,浙江杭州310014 [4]衢州巨化锦纶有限责任公司,浙江衢州324000

出　　处：《化学反应工程与工艺》2024年第4期289-297,共9页Chemical Reaction Engineering and Technology

基　　金：浙江大学衢州研究院科技计划项目(IZQ2022KJ3011);衢州市科技计划项目(2022K05,2021F012);浙江省生产制造方式转型示范项目(2207-330851-04-02-952183)。

摘　　要：分别以SiO_(2),TiO_(2),ZrO_(2)和Al_(2)O_(3)为载体,采用浸渍法负载Keggin型磷钨酸,制备了一系列不同负载量的催化剂。通过红外光谱(FT-IR)、X射线衍射(XRD)、扫描电镜(SEM)和程序升温脱附(NH3-TPD)等表征手段分析催化剂。在无溶剂、减压条件下,使用制得的催化剂,研究了催化剂催化甘露醇脱水反应的性能,考察了催化剂载体种类、磷钨酸负载量、反应时间、反应温度和催化剂用量对甘露醇转化率和脱水产物的影响。结果表明,以30%PW/SiO_(2)为催化剂,催化反应性能较好,较佳的工艺条件是催化剂与甘露醇质量比为0.03,反应温度为170℃,反应时间为2 h,反应体系真空度为0.09 MPa,在此条件下甘露醇的转化率为100.0%,2,5-脱水山梨醇收率为55.7%,1,4-脱水甘露醇收率为9.7%,异甘露醇收率为25.9%,副产物收率为8.5%。A series of supported catalysts with different loading amounts were prepared by impregnating Keggin-type phosphotungstic acid onto SiO_(2),TiO_(2),ZrO_(2),and Al_(2)O_(3) carriers.Characterization methods such as infrared spectroscopy(FT-IR),X-ray diffraction(XRD),scanning electron microscopy(SEM),and temperature programmed desorption(NH_(3)-TPD)were used to analyze the catalyst.The performance of the prepared catalysts in the dehydration of mannitol was studied under solvent-free and depressurized conditions.The effects of catalyst carrier type,phosphotungstic acid loading,reaction time,reaction temperature,and catalyst dosage on the conversion of mannitol and dehydration products were investigated.The results showed that the 30%PW/SiO_(2) catalyst exhibited superior catalytic performance.The optimal process conditions were a catalyst to mannitol mass ratio of 0.03,a reaction temperature of 170℃,a reaction time of 2 h,and a vacuum degree of 0.09 MPa.Under these conditions,the conversion of mannitol was 100.0%,the yield of 2,5-sorbitan was 55.7%,the yield of 1,4-mannitan was 9.7%,the yield of isomannide was 25.9%,and the yield of other components was 8.5%.

关 键 词：甘露醇脱水 催化剂 负载型磷钨酸 反应条件 金属氧化物 

分 类 号：O643.36[理学—物理化学] TQ216[理学—化学]