Effects of Chain Segment Sequence Structures on the Properties of L-Lactide/ε-Caprolactone Copolymers

作　　者：马高琪 潘咏葳 陈志明 梁伟 王良波 李伟民 朱荣华 余承涛 潘鹏举[2,3] MA Gaoqi;PAN Yongwei;CHEN Zhiming;LIANG Wei;WANG Liangbo;LI Weimin;ZHU Ronghua;YU Chengtao;PAN Pengju(Zhejiang Honor Biomaterials Corporation Limited,Taizhou 318000,China;Institute of Zhejiang University-Quzhou,Quzhou 324000,China;College of Chemical and Biological Engineering,Zhejiang University,Hangzhou 310058,China)

机构地区：[1]浙江海诺尔生物材料有限公司,浙江台州318000 [2]浙江大学衢州研究院,浙江衢州324000 [3]浙江大学化学工程与生物工程学院,浙江杭州310058

出　　处：《化学反应工程与工艺》2024年第4期324-332,共9页Chemical Reaction Engineering and Technology

基　　金：国家自然科学基金项目(52103020);浙江省自然科学基金项目(2022C01049)。

摘　　要：聚乳酸(PLA)是常见的生物基可降解塑料之一。通过共聚改性,引入柔性链段[如聚己内酯(PCL)],可以改善PLA质脆和韧性差的问题,但PLA共聚物链段序列结构与其结晶和机械性能的关系不明确。本工作制备了聚(丙交酯-co-己内酯)(PLCL)无规共聚物和PLA-PCL-PLA(L-C-L)三嵌段共聚物,研究分子链序列结构对共聚物结晶性能的影响。结果表明,随着己内酯(CL)比例的提高,PLCL中PLA链段的平均序列长度变短,其结晶速率和结晶度迅速降低,使其杨氏模量降低、断裂应变增大。与之不同的是,L-C-L的序列结构不变,其结晶速率和结晶度无明显变化,但杨氏模量降低、断裂应变增大,韧性提高。Polylactic acid(PLA)is one of the common biodegradable plastics.Copolymerization modification to introduce flexible chain segments(such as polycaprolactone,PCL)can improve the brittleness and poor flexibility of PLA,but the relationship between the chain segment sequence structures of PLA copolymers and their crystallization or mechanical properties is unclear.The poly(lactide-co-caprolactone)(PLCL)random copolymers and PLA-PCL-PLA(L-C-L)triblock copolymers were synthesized,and the effect of the chain segment sequence structures on the crystallization of the copolymers was investigated.The results showed that with the increase of caprolactone proportion,the average sequence length of PLA segment in PLCL shortens,and the crystallization rate and crystallinity of PLCL decreased dramatically,resulting in the decrease of Young’s modulus and the increase of fracture strain.Conversely,the chain segment sequence structures of do not change,nor do its crystallization rate and crystallinity.However,the Young’s modulus of L-C-L decreases and the fracture strain increases,showing the improvement of flexibility.

关 键 词：聚合 聚乳酸 结晶 机械性能 