黄麻/粘胶/水性聚氨酯包装材料制备及优化  

Optimization of the preparation technology of jute/viscose/waterborne polyurethane packaging materials

作　　者：武柳君 陈蔚翔 谢丽梅 周迎春 张斌[1] 郁崇文[1] WU Liujun;CHEN Weixiang;XIE Limei;ZHOU Yingchun;ZHANG Bin;YU Chongwen(College of Textiles,Donghua University,Shanghai 201620,China;Hunan South Original New Material Co.,Ltd.,Changsha 410600,China;Hunan Xiangnan Jute Technology Institute Co.,Ltd.,Chenzhou 423000,China)

机构地区：[1]东华大学纺织学院,上海201620 [2]湖南南源新材料有限公司,长沙410600 [3]湖南省湘南黄麻科技研究院有限公司,湖南郴州423000

出　　处：《现代纺织技术》2024年第9期65-72,共8页Advanced Textile Technology

基　　金：国家现代农业产业技术体系项目(CARS-16);上海市现代纺织前沿科学研究基地项目。

摘　　要：为了缓解塑料包装袋引起的环境污染问题,采用可生物降解的黄麻落麻纤维与粘胶纤维混合并梳理成网,选用水性聚氨酯作为黏合剂将纤维网热压成型,制备了黄麻/粘胶/水性聚氨酯包装材料,并对其进行性能测试和工艺优化。探究原料质量混合比、克重、热压参数对包装材料拉伸强力的影响,并依据单因素分析结果对热压工艺进行正交试验,结果表明:当热压温度为160℃、热压时间为20 s、压强为5 MPa时,包装材料的纵、横向断裂强力分别为126.0、82.6 N,满足购物袋的强力要求。制备可降解的麻纤维包装材料代替塑料包装袋是目前重要的研究方向,对于农业和农村经济的发展具有重要意义。Plastic,with its light weight,high strength and corrosion resistance,is widely used in aerospace,military,agriculture,industry and daily life.At present,most plastic bags commonly used in the market are made of polyethylene,and their wastes are difficult to degrade and pollute the environment,which will affect human health.Therefore,it is an important research direction to explore packaging materials with simple preparation process,low production cost and biodegradability to replace plastic bags.This study mainly explored the preparation technology and performance test of packaging materials.Biodegradable jute noil fiber and viscose were mixed and carded into a net.After needling,water-based polyurethane powder was evenly spread on the mixed fiber net of needled jute and viscose,and then hot-pressed to prepare jute/viscose/water-based polyurethane packaging materials,and the performance test and process optimization were carried out.Firstly,the effects of different mixing ratios of raw materials and gram weight on the mechanical properties of packaging materials were explored.The results show that the breaking strength of the material is the highest when the weight is similar and the ratio of jute/viscose/waterborne polyurethane is 30∶50∶20.Under the same gram weight,the influence of the change of the ratio of viscose to waterborne polyurethane on the tensile properties of the samples with a certain jute fiber content was compared.The results show that the breaking strength of the material is the highest when the ratio of jute/viscose/waterborne polyurethane is 40∶35∶25.With the increase of the proportion of waterborne polyurethane,the breaking strength of the samples increases gradually.It shows that waterborne polyurethane can improve the tensile properties of materials in a certain range.Secondly,the influence of hot pressing process parameters on the properties of jute/viscose/waterborne polyurethane packaging materials was studied.The results show that the strength of packaging materials first increa

关 键 词：黄麻落麻 粘胶 水性聚氨酯 非织造 包装材料 