基于低碱度精炼渣的Q390C钢水洁净度控制实践  

Practice of Controlling the Cleanliness of Q390C Steel Under low Alkalinity Refining Slag

作　　者：姜新岩 王兴 李杰 陈方 Jiang Xinyan;Wang Xing;Li Jie;Chen Fang(Shaanxi Steel Group Industrial Innovation Research Institute Co.,Ltd.,Hanzhong Shaanxi 723000,China)

机构地区：[1]陕钢集团产业创新研究院有限公司,陕西汉中723000

出　　处：《山西冶金》2024年第8期161-163,共3页Shanxi Metallurgy

摘　　要：针对低合金高强度中厚钢板Q390C钢在低碱度精炼渣下钢水洁净度进行了研究,结果表明,渣系组分w(CaO)=43%~48%、w(SiO_(2))为12%~15%、w(Al_(2)O_(3))为23%~27%、w(MgO)为3%~7%、碱度(CaO与SiO2质量比)为3~4时,渣系完全处于液相区,钢中w[S]≤0.008%,w(T.[O])≤0.0025%,BT类、Ds类夹杂物级别降低,钢水洁净度满足指标要求。A study was conducted on the cleanliness of molten steel under low alkalinity refining slag for Q390C steel plate.The results showed that the slag system component w(CaO)=43%~48%;w(SiO_(2))=12%~15%;w(Al_(2)O_(3))=23%~27%;w(MgO)is 3%~7%.When alkalinity(CaO/SiO_(2))is 3~4,the slag is completely in the liquid phase,and w[S]≤0.008%,w(T.[O])≤0.0025%,the level of BT and Ds inclusions is reduced,and the cleanliness of the molten steel meets the requirements.

关 键 词：Q390C钢 精炼渣 钢水洁净度 

分 类 号：TF734.34[冶金工程—钢铁冶金]