On the Factors Influencing the High Stretch-Flangeability of a Low-Density 1180 MPa Fe-Mn-Al-C-Nbδ-QP Steel  

作　　者：Dan‑Dan Cui Peng Chen Peng‑Fei Wang Xiao‑Wu Li 

机构地区：[1]Department of Materials Physics and Chemistry,School of Materials Science and Engineering,and Key Laboratory for Anisotropy and Texture of Materials(Ministry of Education),Northeastern University,Shenyang 110819,China [2]State Key Laboratory of Rolling and Automation,Northeastern University,Shenyang 110819,China

出　　处：《Acta Metallurgica Sinica(English Letters)》2024年第8期1291-1300,共10页金属学报（英文版）

基　　金：supported by the National Natural Science Foundation of China(Grant Nos.52171108 and 51804072);the Fundamental Research Funds for the Central University(Grant Nos.N2202007 and N2202011);Special thanks are also due to the instrumental or data analysis from Analytical and Testing Center,Northeastern University,China.

摘　　要：Low-densityδ-quenching and partitioning(δ-QP)steels with excellent strength and ductility have been recently developed.However,there are still rare reports on the formability of δ-QP steels,which are critical for satisfying the manufacture of structural parts during the application in automotive industry.In the present work,an 1180 MPa Fe–Mn–Al–C–Nbδ-QP steel with a high ductility was adopted for the stretch–flangeability study.Theδ-QP steel was developed by separated quenching and partitioning processes.A good hole expansion ratio(HER)of 34.9±0.9%was obtained in the quenched steel,but it has been further increased to 52.2%by the tempering treatment.The improved stretch–flangeability was attributed to the enhanced austenite stability and deformation uniformity.On the one hand,the stability of austenite was increased by carbon partitioning during tempering,which reduced crack possibility via the suppression of the fresh martensite formation.On the other hand,the tempering treatment released the internal stress caused by martensitic transformation and reduced the difference in strength among different phases,resulting in an increase in the resistance to crack initiation and propagation.

关 键 词：Hole expansion ratio Low-densityδ-quenching and partitioning(δ-QP)steel Stretch-flangeability Austenite stability Deformation uniformity 

分 类 号：TG142.1[一般工业技术—材料科学与工程]