Nd^(3)+:YAG-Al_(2)O_(3) nanocrystalline transparent ceramics with high inflexion concentration quenching of Nd^(3+) prepared by amorphous crystallization  

作　　者：Xiujuan Wan Guangfan Tan Liang Cai Jie Fu Jianqiang Li Yingchun Zhang 

机构地区：[1]School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China [2]State Key Laboratory of New Ceramics and Fine Processing,School of Materials Science and Engineering,Tsinghua University,Beijing 100080,China [3]State Key Lab for Mesoscience and Engineering,Institute of Process Engineering,Chinese Academy of Sciences,Beijing 100190,China

出　　处：《Journal of Advanced Ceramics》2024年第8期1242-1253,共12页先进陶瓷（英文）

基　　金：This work was financially supported by the National Natural Science Foundation of China(No.51972018).

摘　　要：Rare earth ion-doped Y_(3)Al_(5)O_(12)(YAG)-based transparent ceramics have been used as important laser gain media for a long time,yet the doping concentration of active ions is limited due to concentration quenching,wherein the inflexion concentration quenching of Nd^(3+)is recognized as 1.0 at%.In this work,YAG-Al_(2)O_(3) nanocrystalline transparent ceramics with a concentration of Nd^(3+)(O-5.0 at%)were fabricated via amorphous crystallization,and the crystal structure evolution,morphology,and optical properties were systematically investigated by differential scanning calorimetry(DSC),X-ray powder diffraction(XRD),transmission electron microscopy(TEM),magnetic resonation(MAS),nuclear magnetic resonation(NMR),and fluorescence spectroscopy.The doping of Nd^(3+)can promote the transition of Al[5]and Al[6]to Al[14],indicating improvements in the ability of the amorphous material to form Nd^(3+):Y_(2)O_(3)-Al_(2)O_(3) vitrified beads,and 1.5 at%Nd^(3+):YAG-Al_(2)O_(3) nanocrystalline transparent ceramics can be obtained by crystallization at 1050℃ with a matrix composed of YAG and concomitant δ-Al_(2)O_(3) and θ-Al_(2)O_(3).The nanocrystalline transparent ceramics show an internal transmitance of 89.56%at 1064 nm,and the strongest emission peak corresponds to the energy transfer from 4F_(3/2) to 4l_(11/2) of Nd^(3+)with a fluorescence lifetime of 231μs when pumped by an 808 nm laser.Specifically,spectral broadening begins to occur,indicating the onset of concentration quenching,when the concentration of Nd^(3+)exceeds 1.5 at%,substantially higher than the 1.0 at% observed in YAG ceramics.YAG-Al_(2)O_(3) nanocrystalline transparent ceramics obtained by amorphous crystalization can be utilized as the matrix to increase the inflexion point of doping concentration quenching of Nd^(3+),and this material may have great potential as a laser gain medium.

关 键 词：Y_(3)Al_(5)O_(12)(YAG)-Al_(2)O_(3) NANOCRYSTALLINE transparent ceramics laser gain medium Nd^(3+) 