聚丙烯纤维增强水利堤坡轻骨料混凝土的抗压性能  

Compressive Performance of Polypropylene Fiber Reinforced Lightweight Aggregate Concrete for Water Conservancy Embankment Slopes

作　　者：张明远 ZHANG Ming-yuan(Pingyuan County Water Conservancy Development Center,Dezhou 253100,Shandong,China)

机构地区：[1]平原县水利事业发展中心,山东德州253100

出　　处：《合成纤维》2024年第11期85-87,91,共4页Synthetic Fiber in China

摘　　要：为探究聚丙烯纤维对轻骨料混凝土抗压性能的影响,设计不同纤维掺量,分别制备聚丙烯纤维轻骨料混凝土,养护龄期取7、14、21、28、60 d并分别测定各组混凝土在不同龄期下的抗压强度。结果显示,聚丙烯纤维掺入后,各组轻骨料混凝土的抗压强度均会得到不同程度提升,且抗压强度均大致表现为随聚丙烯纤维掺量增加而前期增加、后期降低的发展趋势,其中掺加0.9 kg/m^(3)聚丙烯纤维时抗压强度达到最佳水平。试验表明,聚丙烯纤维掺入后混凝土破坏形态出现改变,显著提升混凝土早期强度,且有效改善混凝土脆性。In order to explore the influence of polypropylene fibers on the compressive performance of light⁃weight aggregate concrete,different fiber dosages were designed,and polypropylene fiber lightweight aggre⁃gate concrete was prepared separately.The curing ages were set at 7、14、21、28、60 d,and the com⁃pressive strength of each group of concrete were measured at different ages.The results show that after the addition of polypropylene fibers,the compressive strength of each group of lightweight aggregate concrete will be improved to varying degrees,and the compressive strength generally shows a development trend of increasing in the early stage and decreasing in the later stage with the increase of polypropylene fiber con⁃tent.Among them,the compressive strength reaches the optimal level when 0.9 kg/m^(3) polypropylene fibers are added.Experiments have shown that the addition of polypropylene fibers changes the failure mode of concrete,which significantly enhances its early strength and effectively improves its brittleness.

关 键 词：水利堤坡 轻骨料混凝土 聚丙烯纤维 抗压性能 

分 类 号：TQ342.62[化学工程—化纤工业] TV431.3[水利工程—水工结构工程]