小方坯连铸机提高拉速攻关实践  

Practice of Improving Casting Speed of Billet Continuous Casting Machine

作　　者：张祥远 Zhang Xiangyuan(Fujian Quanzhou Minguang Iron and Steel Co.,Ltd.,Quanzhou 362411,Fujian)

机构地区：[1]福建泉州闽光钢铁有限责任公司,福建泉州362411

出　　处：《福建冶金》2024年第6期51-53,共3页Fujian Metallurgy

摘　　要：针对福建泉州闽光钢铁有限责任公司炼钢厂现有160 mm×160 mm方坯连铸机生产设备条件,通过提高结晶器冷却强度、优化二次冷却制度、增加切割前冷却装置等措施进行高拉速技术改造,成功将铸机生产平均拉速由2.6 m/min提高至3.2 m/min,最高拉速达到3.45 m/min。In response to the existing production equipment conditions of the 160 mm×160 mm billet continuous casting machine at the steelmaking plant of Fujian Quanzhou Minguang Iron and Steel Co.,Ltd.,high casting speed technology transformation was carried out by improving the cooling intensity of the crystallizer,optimizing the secondary cooling system,and adding cooling devices before cutting.The average casting speed of the casting machine was successfully increased from 2.6 m/min to 3.2 m/min,with a maximum casting speed of 3.45 m/min.

关 键 词：小方坯 高拉速 二次冷却 切割漏钢 

分 类 号：TF341.6[冶金工程—冶金机械及自动化]