Effect of gradient microstructure on the bendability of AZ31 alloy sheet  

作　　者：Lintao Liu Jieyu Li Shengwen Bai Bin Jiang Chao He Jianxin Zhou Guangsheng Huang Dingfei Zhang Fusheng Pan 

机构地区：[1]National Engineering Research Center for Magnesium Alloys,Chongqing University,Chongqing 400044,China [2]College of Materials Science and Engineering,Chongqing University,Chongqing 400044,China [3]Chongqing Academy of Science and Technology,Chongqing 401123,China

出　　处：《Journal of Materials Science & Technology》2024年第11期143-154,共12页材料科学技术（英文版）

基　　金：National Key Research and Development Program of China(Project No.2021YFB3701000);financial support of the National Natural Science Foundation of China(Project Nos.52101124,U21A2048);Independent Research Project of State Key Laboratory of Mechanical Transmissions(Project No.SKLMT-ZZKT-2022M12).

摘　　要：Extensive researches have elucidated the pronounced benefits of gradient microstructures for the me-chanical properties of metallic materials.However,the ramifications of gradient microstructures on formability,particularly regarding their effects on bendability,remain inadequately understood.In this work,the effects of gradient microstructure on the bendability of AZ31 Mg alloy sheet are systematically investigated by comparing the microstructure evolution and strain distribution in the sheets with uni-form microstructure(grain size=12.8 μm and 91.3 μm)and gradient microstructure(grain size=11.5-75.4 μm).The results show that the bendability of the sheet with gradient microstructure is significantly improved when the fine grains(FGs)are placed at the outer side(TBE-FG sample)and the bendability is increased by 93.1%compared to the sample with fine and uniform microstructure(CE-FG sample).With coarse grains(CGs)placed at the inner side,the strain at the compressive region of the TBE-FG sample is higher than its counterparts,while the tensile strain at the extended region is lowest among the four samples.Quasi-in-situ bending experiments reveal that the CGs at the inner side of the TBE-FG sample undergo more twinning.Moreover,the increment of residual dislocation density at the outer side of the TBE-FG sample is lower than those of other samples,which extends the bending potential.This work provides a novel perspective to improve the bendability of the Mg alloy sheet.

关 键 词：Gradient microstructure BENDABILITY Strain distribution Quasi-in-situ bending 

分 类 号：TG146.22[一般工业技术—材料科学与工程]