Microstructure and Mechanical Properties of Al_(2)O_(3p)/AZ91 Magnesium Matrix Laminated Material Adjusted by Freezing Temperature  

作　　者：Ze-Xin Bai Kun-Kun Deng Ze-Qi Du Kai-Bo Nie Chao Xu Quan-Xin Shi 

机构地区：[1]Shanxi Key Laboratory of Advanced Magnesium-based Materials,College of Materials Science and Engineering,Taiyuan University of Technology,Taiyuan 030024,China [2]School of Materials Science and Engineering,Harbin Institute of Technology,Harbin 150001,China

出　　处：《Acta Metallurgica Sinica(English Letters)》2024年第11期1819-1829,共11页金属学报（英文版）

基　　金：supported by the National Key Research and Development Program for Young Scientists(Grant No.2021YFB3703300);the National Natural Science Foundation of China(Grant Nos.52271109 and 52001223);the Major Special Plan for Science and Technology in Shanxi Province(Grant No.202201050201012);the Special Fund Project for Guiding Local Science and Technology Development by the Central Government(Grant No.YDZJSX2021B019)。

摘　　要：The Al_(2)O_(3)laminated preforms with different layers thickness were prepared by freezing casting in present work.Then,the Al_(2)O_(3p)/AZ91 magnesium matrix laminated materials were obtained by infiltrating the AZ91 alloy melt into the Al_(2)O_(3)laminated preform based on pressure infiltration process.Subsequently,the influence of freezing temperature on the microstructure,mechanical properties and fracture behavior of magnesium-based laminates was investigated.The results indicated that with the decrease of freezing temperature,the thickness of Al_(2)O_(3)layers decreases gradually,the number of layers increases obviously,and the interlayers spacing decreases.Accompanied with the decrease of interlayers spacing,the size of Mg17Al12 phase precipitated in the AZ91 alloy layers was refined,and the compression strength and strain were both improved obviously.The micro-cracks initiated in Al_(2)O_(3)layers during loading process,while the AZ91 layers could effectively suppress the initiation and propagation of micro-cracks.Furthermore,the changing layers structure influenced by the decrease of freezing temperature had significant inhibiting effect on the initiation and propagation of micro-cracks,which endowed the Al_(2)O_(3p)/AZ91 magnesium matrix laminated materials with better strength and toughness.Notably,the best compression properties of Al_(2)O_(3p)/AZ91 magnesium matrix laminated materials could be obtained at the freezing temperature of−50℃,the compression strength and elastic modulus of which were the 160%and 250%of monolithic AZ91 alloy,respectively.

关 键 词：Bio-inspired composites Freeze-casting Mechanical properties Metal matrix composites 

分 类 号：TB33[一般工业技术—材料科学与工程]