Cold sintered BaTiO_(3)–poly(ether imide)nanocomposites with superior comprehensive performances  

作　　者：Xinyi Li Li Li Mingming Si Xiaoqian Tai Hong Wang Jing Guo 

机构地区：[1]State Key Laboratory for Mechanical Behavior of Materials&School of Materials Science and Engineering,Xi’an Jiaotong University,Xi’an 710049,China [2]Guangdong Provisional Key Laboratory of Functional Oxide Materials and Devices,Southern University of Science and Technology,Shenzhen 518055,China [3]Department of Materials Science and Engineering&Shenzhen Engineering Research Center for Novel Electronic Information Materials and Devices,Southern University of Science and Technology,Shenzhen 518055,China

出　　处：《Journal of Advanced Ceramics》2024年第9期1453-1460,共8页先进陶瓷（英文）

基　　金：supported by the Natural Science Foundation of Shaanxi Province,China(No.2024JC-YBMS-349);the Guangdong Provincial Key Laboratory Program(No.2021B1212040001);the staff at the Instrument Analysis Centre of Xi’an Jiaotong University for the XRD,FT-IR,and TEM measurements.We also thank Xiaohua Cheng from the School of Materials Science and Engineering,Xi’an Jiaotong University for SEM measurements.

摘　　要：With the rapid development of the electronics industry,the demand for dielectric materials with high permittivities,low losses,and excellent electrical breakdown strengths prepared via low-temperature fabrication techniques is increasing.Herein,we propose a one-step cold sintering process route to improve the comprehensive performance of BaTiO_(3)−based ceramics by integrating polyetherimide(PEI).Dense BaTiO_(3)–PEI nanocomposites can be prepared via a cold sintering process at 250℃ using Ba(OH)_(2)∙8H_(2)O and H_(2)TiO_(3) as the transient liquid phase.The grain growth of BaTiO_(3) is inhibited,and thin PEI layers less than 10 nm in size are located at the grain boundaries.The dissolution‒precipitation process triggered by the transient liquid phase and viscous flow assisted by PEI dominates the cold sintering mechanism of the(1−x)BaTiO_(3)–xPEI nanocomposites.The dielectric properties are stable over a broad temperature range up to 200℃.Compared with BaTiO_(3),80%BaTiO_(3)–20%PEI has superior performance,with a relative permittivity of 163 and a low dielectric loss of 0.014,and the electrical breakdown strength is increased by 80.65%compared with BaTiO_(3).Overall,the cold sintering process provides a potential way to develop dielectric nanocomposites with excellent comprehensive performance.

关 键 词：cold sintering process(CSP) dielectrics BaTiO_(3) ceramic-polymer composites 

分 类 号：TQ426[化学工程] X703[环境科学与工程—环境工程]