聚变堆真空室T型焊缝相控阵超声检测技术分析  

Analysis of phased array ultrasonic inspection technology for T-welds in vacuum chamber of fusion reactor

作　　者：陈韧 汪月琴 王锐[2,3] 吉海标 李成文 CHEN Ren;WANG Yueqin;WANG Rui;JI Haibiao;LI Chengwen(School of Mechanics and Optoelectronic Physics,Anhui University of Science and Technology,Huainan 230031,China;Institute of Plasma Physics,HFIPS,Chinese Academy of Sciences,Hefei 230031,China;Anhui Province Key Laboratory of Special Welding Technology,Huainan 232000,China)

机构地区：[1]安徽理工大学力学与光电物理学院,淮南230031 [2]中国科学院合肥物质科学研究院,合肥230031 [3]特种焊接安徽省重点实验室,淮南232000

出　　处：《无损检测》2024年第11期1-4,共4页Nondestructive Testing

摘　　要：作为聚变堆装置中的核心部件,真空室的焊缝坡口要求全焊透,对焊接质量有着严格要求。针对聚变堆真空室T型焊缝,使用相控阵超声检测的方式控制焊缝质量。然而焊缝粗晶的组织特征和真空室的复杂结构给相控阵超声检测带来了挑战。针对此问题,首先通过CIVA软件对探头焦点和焦柱尺寸进行仿真计算,并根据计算结果为检测方案设计提供参考,然后设计了使用双面阵探头在腹板侧面激发扇形扫查,结合线阵探头在翼板外侧面激发角度垂直于熔合线的线性扫查的检测方案,对预埋有典型焊接缺陷的模拟试块进行了检测,实现了缺陷的全检出。该检测方案可为T型焊缝检测的实际应用提供参考。As the core component of the fusion reactor device,the weld bevel of the vacuum chamber requires full weld penetration,and the welding quality has strict requirements.In this paper,phased array ultrasonic inspection was used to control the quality of T-shaped welds in the vacuum chamber of a fusion reactor.However,the coarse crystalline organization of the weld and the complex structure of the vacuum chamber brought challenges to the phased array ultrasonic inspection.In this paper,the simulation calculation of the probe focus and focal column size was performed by CIVA software,and the results provided reference for the design of the inspection scheme,and then the full detection of defects was achieved by using the inspection scheme of fan sweeping excited by a double-sided array probe on the side of the web,and linear sweeping with an angle perpendicular to the fusion line excited by a line array probe on the outer side of the wing plate to inspect the demonstration block with typical weld defects.The inspection program can provide guidance for the inspection of T-welds in practical applications.

关 键 词：真空室 相控阵超声 T型焊缝 

分 类 号：TG115.28[金属学及工艺—物理冶金]