Phase structure evolution and coercivity mechanism of high-Co containing permanent magnets  

作　　者：Min Huang Yong Ding Zhihe Zhao Chunguo Wang Bo Zhou Lei Liu Yingli Sun Aru Yan 黄敏;丁勇;赵之赫;王春国;周波;刘雷;孙颖莉;闫阿儒(CISRI & NIMTE Joint Innovation Center for Rare Earth Permanent Magnets,CAS Key Laboratory of Magnetic Materials and Devices,Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology,Ningbo Institute of Materials Technology and Engineering,Chinese Academy of Sciences,Ningbo 315201,China;University of Chinese Academy of Sciences,Beijing 100049,China)

机构地区：[1]CISRI & NIMTE Joint Innovation Center for Rare Earth Permanent Magnets,CAS Key Laboratory of Magnetic Materials and Devices,Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology,Ningbo Institute of Materials Technology and Engineering,Chinese Academy of Sciences,Ningbo 315201,China [2]University of Chinese Academy of Sciences,Beijing 100049,China

出　　处：《Chinese Physics B》2024年第11期403-410,共8页中国物理B（英文版）

基　　金：Project supported by National Key R&D Program of China(Grant No.2021YFB3803003);Youth Innovation Promotion Association CAS(Grant No.2023311).

摘　　要：The phase structure and magnetic properties of high-Co containing permanent magnets with high thermal stability have been systematically studied in this work.It is abnormal that the coercivity of annealed samples was slightly lower than that of sintered samples,while the coercivity was usually enhanced after annealing in conventional Nd–Fe–B samples.Further analysis showed that in addition to RE_(2)(Fe,Co)_(14)B main phase and RE-rich grain boundary phase,there were also new Co-rich magnetic phases located in the grain boundary.During annealing,the phase structures of high-Co containing magnets were readjusted,especially the increasing Co-rich magnetic phase and emerging RE-rich particles precipitated from the main phase.Eventually,the isolated RE-rich particles would act as the pinning center of the domain wall movement in demagnetization process.It was confirmed that the coercivity of annealed high-Co containing magnets was controlled by both nucleation and pinning.Pinning mechanism can partially compensate for the weakening of magnetic isolation due to increased Co-rich magnetic phase,which explained the moderate decrease in coercivity of annealed high-Co containing magnets.The discovery of new coercivity mechanism contributed to in-depth understanding of high-Co containing magnets.

关 键 词：Co-rich phase PINNING coercivity mechanism high-Co containing magnets 