Preparation of Y_(2)O_(3)Transparent Ceramics by Colloidal Forming Method Based on the Synergistic Effect of Double Dispersants

作　　者：曲胜箫 穆浩洁 杨亮 李晓东 史树君 孙旭东 QU Shengxiao;MU Haojie;YANG Liang;LI Xiaodong;SHI Shujun;SUN Xudong(Key Laboratory for Anisotropy and Texture of Materials(Ministry of Education),Research Center for Advanced Ceramic Materials,School of Materials Science and Engineering,Northeastern University,Shenyang 110819,China;Northeastern University Foshan Graduate School,Foshan 528311,China)

机构地区：[1]东北大学材料科学与工程学院,先进陶瓷材料研究中心,材料各向异性与织构教育部重点实验室,沈阳110819 [2]东北大学佛山研究生院,佛山528311

出　　处：《人工晶体学报》2024年第11期1981-1989,共9页Journal of Synthetic Crystals

基　　金：国家自然科学基金(52472065);潍坊市科学技术发展计划(2021ZJ1210)。

摘　　要：分散良好的高固含量悬浮液是胶态成型方法获得微观结构均匀且尺寸精确的陶瓷素坯的前提,也是制备高光学质量透明陶瓷以满足光学窗口用需求的基础。本文旨在通过柠檬酸三铵(TAC)和聚丙烯酸铵(A40)两种分散剂的协同作用来提高Y_(2)O_(3)悬浮液的分散稳定性。研究了双分散剂混合比例对Y_(2)O_(3)悬浮液稳定性及成型素坯微观结构的影响,确定了双分散剂体系在提高Y_(2)O_(3)悬浮液固含量和稳定性方面的优势。结果表明,在TAC和A40的质量比为7∶3条件下所制备的Y_(2)O_(3)悬浮液固含量可达38%(体积分数),成型的素坯微观结构均匀且颗粒致密堆积,素坯经1800℃真空烧结后得到了直径为9 mm、厚度为1 mm的Y_(2)O_(3)透明陶瓷,在800 nm处透过率为70.34%。The preparation of a well-dispersed,high solids content suspension is the foundation for colloidal forming methods to achieve ceramic green bodies with a uniformly microstructure,and meet the application requirements of various optical window materials.This article aims to enhance the dispersion stability of Y_(2)O_(3)suspension by utilizing the synergistic effect of two dispersants,namely triammonium citrate(TAC)and ammonium polyacrylate(A40).The influence of the mixing ratio of two dispersants on the stability of Y_(2)O_(3)suspension and the microstructure of formed green bodies were mainly investigated,and the advantages of the dual dispersant system in improving the solid content and stability of Y_(2)O_(3)suspension were determined.The results show that the solid content of Y_(2)O_(3)suspension could reach 38%(volume fraction)under the condition of TAC to A40 mass ratio of 7∶3.A uniformly microstructure and densely packed particle was achieved.Y_(2)O_(3)transparent ceramics with a diameter of 9 mm and a thickness of 1 mm were obtained by vacuum sintering at 1800℃,with a transmittance of 70.34%at 800 nm.

关 键 词：氧化钇 透明陶瓷 分散剂 胶态成型 真空烧结 