C100机制砂免压蒸管桩混凝土配制技术研究  

Research on concrete preparation technology of C100 machine-made sand non-autoclaved pipe pile

作　　者：高超 陈鹏 王晶 卢传泰 汤国芳 李健 高麒 GAO Chao;CHEN Peng;WANG Jing;LU Chuantai;TANG Guofang;LI Jian;GAO Qi(China Academy of Building Research,Beijing 100013,China;State Key Laboratory of Building Safety and Built Environment,Beijing 100013,China;National Construction Engineering Technology Research Center,Beijing 100013,China;Jiangsu Chengyi Pile Industry Technology Development Co.,Ltd.,Xuxhou 221000,China;Jiangsu Chengyi Engineering Technology Research Institute Co.,Ltd.,Xuxhou 221000,China;Jiangsu Chengyi Residential Industrial Technology Development Co.,Ltd.,Xuxhou 221131,China)

机构地区：[1]中国建筑科学研究院有限公司,北京100013 [2]建筑安全与环境国家重点实验室,北京100013 [3]国家建筑工程技术研究中心,北京100013 [4]江苏诚意桩业科技发展有限公司,江苏徐州221000 [5]江苏诚意工程技术研究院有限公司,江苏徐州221000 [6]江苏诚意住宅工业科技发展有限公司,江苏徐州221131

出　　处：《混凝土》2024年第11期155-158,共4页Concrete

基　　金：“十三五”国家重点研发计划项目“混凝土制品微结构加速形成机制与损伤控制机理”(2017YFB0310001)。

摘　　要：为实现节能低碳的生产工艺,推广应用C100机制砂免压蒸管桩,采用由I级粉煤灰、超细粉煤灰、硅灰组成的管桩专用矿物掺合料和机制砂试配免压蒸管桩混凝土,研究了矿物掺合料掺量、胶凝材料总量、水胶比、静停时间、升温速率对管桩混凝土性能的影响。结果表明:通过优化配合比设计参数和蒸养制度配制出适用于开模人工布料方式的免压蒸管桩混凝土,离心成型后内壁质量较好,蒸养脱模、3 d、28 d抗压强度分别超过95 MPa、100 MPa、105 MPa,蒸养脱模、28 d氯离子迁移系数分别低于4×10^(-12)m^(2)/s、3×10^(-12)m^(2)/s。In order to realize the production process of energy saving and low carbon,C100 machine-made sand non-autoclaved pipe pile are popularizing and applying.The special mineral admixtures for pipe pile mainly contains I fly ash,ultra-fine fly ash,silica fume and machine-made sand were used to test and mix the concrete for non-autoclaved pipe pile.The effects of the mineral admixtures,the total amount of cementitious materials,the water-cement ratio,the static stop time and the heating rate on the performance of the concrete for pipe piles were studied.The results show that the non-autoclaved pipe pile concrete suitable for manual distribution mode of mold opening was prepared by optimizing the mix design parameters and steam curing system,the quality of the inner wall after centrifugal molding is good.The compressive strength of steam curing demoulding,3 d and 28 d exceeds 95 MPa,100 MPa and 105 MPa respectively,and the chloride ion migration coefficient of steam curing demoulding and 28 d is lower than 4×10^(-12) m^(2)/s、3×10^(-12) m^(2)/s。

关 键 词：C100 机制砂免压蒸管桩混凝土 配合比设计 蒸养制度 

分 类 号：TU528.7[建筑科学—建筑技术科学]