高导热硫化胶囊在12R22.5CST11318PR全钢子午线轮胎生产中的应用  

Application of High Thermal Conductivity Vulcanization Capsules in Production of 12R22.5CST11318PR All-steel Radial Tire

作　　者：王俊霞 王亮 武茂军 王业杰 WANG Junxia;WANG Liang;WU Maojun;WANG Yejie(Pulin Chengshan(Shandong)Tire Co.,Ltd,Rongcheng 264300,China)

机构地区：[1]浦林成山(山东)轮胎有限公司,山东荣成264300

出　　处：《轮胎工业》2024年第12期754-758,共5页Tire Industry

摘　　要：研究高导热硫化胶囊在12R22.5CST11318PR全钢子午线轮胎生产中的应用,并与普通硫化胶囊进行对比。结果表明:高导热硫化胶囊的热导率比普通硫化胶囊增大47%;采用高导热硫化胶囊可将内蒸汽温度由210℃降至198℃,同时硫化时间缩短,轮胎的耐久性能和高速性能提高,单胎能源消耗降低;高导热硫化胶囊的使用寿命更长。The application of high thermal conductivity vulcanization capsules in the production of 12R22.5CST11318PR all-steel radial tire production was studied and compared with ordinary vulcanization capsules.The results showed that the thermal conductivity of high thermal conductivity vulcanization capsules was higher than that of the ordinary vulcanization capsules.The use of high thermal conductivity vulcanization capsules could reduce the internal steam temperature from 210℃to 198℃,shorten the vulcanization time,improve the durability and high-speed performance of the tire,and reduce the single tire energy consumption.The service life of high thermal conductivity vulcanization capsules was longer.

关 键 词：全钢子午线轮胎 硫化胶囊 热导率 高速性能 耐久性能 

分 类 号：TQ336.1[化学工程—橡胶工业]