等离子体协同过氧化氢活化体系对纯棉水刺非织造布的练漂处理  

Scouring and bleaching of cotton nonwoven fabrics using plasma-assisted hydrogen peroxide activation system

作　　者：肖鑫 李伟 卢润 姜会钰 李青[1,3] XIAO Xin;LI Wei;LU Run;JIANG Huiyu;LI Qing(School of Textile Science and Engineering,Wuhan Textile University,Wuhan,Hubei 430200,China;Yantai Yelin Textile Printing&Dyeing Co.,Ltd.,Yantai,Shandong 261400,China;Hubei Key Laboratory of Biomass Fibers and Eco-dyeing&Finishing,Wuhan Textile University,Wuhan,Hubei 430200,China)

机构地区：[1]武汉纺织大学纺织科学与工程学院,湖北武汉430200 [2]烟台业林纺织印染有限责任公司,山东烟台261400 [3]武汉纺织大学生物质纤维与生态染整湖北省重点实验室,湖北武汉430200

出　　处：《纺织学报》2024年第12期118-127,共10页Journal of Textile Research

基　　金：国家自然科学基金青年基金项目(52303062);生物质纤维与生态染整湖北省重点实验室开放课题(STRZ202303);湖北省科技厅重点研发计划(助企纾困及包保联2022BAD012)。

摘　　要：针对纯棉水刺非织造布练漂温度高、碱性强、纤维损伤严重等问题,先对其进行等离子体处理,再构建过氧化氢/五乙酰葡萄糖(H_(2)O_(2)/PAG)体系进行练漂处理。对处理前后样品的表面元素组成、微观形貌和结晶结构进行表征,探究等离子体的助漂机制。通过单因素实验分析了等离子体处理时间、H_(2)O_(2)和PAG浓度、NaHCO_(3)浓度、练漂温度和时间对非织造布白度的影响,优化了处理工艺。结果表明:与NaOH/H_(2)O_(2)体系练漂效果相近时,H_(2)O_(2)/PAG体系能将处理温度降低20℃,pH值维持在5~7,在此基础上引入等离子体可进一步将H_(2)O_(2)浓度降低50%,或将练漂时间缩短一半;等离子体通过刻蚀纤维表面,增加含氧基团与无定形区比例,使漂液更易渗透纤维,从而提高练漂效率。优化工艺为:等离子体处理时间5 min,漂液中含30 mmol/L H_(2)O_(2),7.5 mmol/L PAG,30 mmol/L NaHCO_(3),在70℃处理30 min。此工艺条件下处理的样品白度可提升23.8%,水滴铺展时间小于1 s,该效果超过了H_(2)O_(2)/PAG体系与H_(2)O_(2)/NaOH体系的练漂效果。Objective As a healthy and environmentally friendly cotton fiber product,cotton nonwoven fabrics have been widely applied in various fields.All natural cotton fiber contains pigment impurities and needs to be scoured and bleached.Hydrogen peroxide(H_(2)O_(2))bleaching is usually carried out in high-temperature and strong-alkali environment.The H_(2)O_(2)/activator system can effectively reduce the bleaching temperature and alkalinity.However,partial activators possess ecotoxicity.This research aims to explore for cleaner and more effective scouring and bleaching methods.Method Firstly,the cotton nonwoven fabric was pre-treated with a plasma cleaning machine for 5 min.Subsequently,the fabric was immediately immersed in H_(2)O_(2)/PAG bleaching solution for treatment at 70℃ for 30 min in a constant-temperature dyeing machine.After the treatment,the fabric was squeezed and laundered thoroughly before being air-dried.The solution mentioned above contained H_(2)O_(2),PAG,NaHCO 3,and EDTA-2Na.The fabric′s whiteness and hydrophilicity were tested to evaluate the bleaching and scouring performance,respectively.The influences of plasma treatment on the chemical structure of cotton fiber were analyzed using X-ray photoelectron spectrum,scanning electron microscopy,and X-ray diffraction.Results For achieving comparable bleaching effect via the NaOH and H_(2)O_(2)routes,the H_(2)O_(2)/PAG system was able to reduce the bleaching temperature by 20℃and to maintain the pH value at 5-7.On this basis,the introduction of plasma was shown to further reduce the H_(2)O_(2)concentration by 50%or shorten the bleaching time by half,and the degree of polymerization was decreased by 3.6%.Plasma treatment significantly improved the hydrophilicity of cotton nonwoven fabrics.Specifically,the contact angle of water droplets reduced from 106.7°to 38.1°,and the wicking height within 30 min increased from 0 to 5.7 cm.Analysis of the X-ray energy spectrum indicated that both the content of oxygen elements and the number of polar oxygen-con

关 键 词：等离子体 低温练漂 棉非织造布 过氧化氢 功能纺织品 

分 类 号：TS192.5[轻工技术与工程—纺织化学与染整工程]