辽宁省北票地区沸石改性研究  

Study on Modification of Zeolite from Beipiao Area of Liaoning Province

在线阅读下载全文

作  者:刘森[1] 范天博[1] 李秋彤 张欣爱 焦立强 郭洪范[1] 李雪[1] LIU Sen;FAN Tianbo;LI Qiutong;ZHANG Xin'ai;JIAO Liqiang;GUO Hongfan;LI Xue(Shenyang University of Chemical Technology,Shenyang Liaoning 113001,China)

机构地区:[1]沈阳化工大学,辽宁沈阳110142

出  处:《辽宁化工》2024年第12期1820-1823,1828,共5页Liaoning Chemical Industry

基  金:国家重点研发计划“固废资源化”重点专项资助(项目编号:2020YFC1909300);辽宁省教育厅项目资助(项目编号:LJKZ0431);辽宁省教育厅项目资助(项目编号:L2013169);国家自然基金资助(项目编号:61102041);辽宁省高校创新团队支撑计划资助(项目编号:2013010);国家科技支撑计划资助(项目编号:2013BAB09B01);辽宁省精细化工协同创新中心资助项目资助;辽宁省自然基金资助(项目编号:201602582);辽宁省高等学校创新人才支持计划资助(项目编号:LR2018078);辽宁省自然科学基金材料联合基金资助(项目编号:20180510007);辽宁省自然科学基金指导计划项目资助(项目编号:2019ZD0075)。

摘  要:辽宁省北票地区沸石资源丰富,但长期以来加工利用水平较低。为改善其比表面积、吸氨量等性能,采用了不同方法对沸石进行了改性,利用比表面积测定仪测定比表面积和化学法滴定吸氨量。结果表明:采用1 mol·L^(-1) Na Cl溶液改性沸石,改性时间20 h的沸石吸氨量可以达到182.1 mmol·(100g)^(-1),比表面积为16.499 m^(2)·g^(-1);HCl溶液改性沸石,在1.5 mol·L^(-1) HCl溶液浸泡改性的沸石有较好的比表面积,可以达到63.577 m^(2)·g^(-1),吸氨量为162.9 mmol·(100 g)^(-1);NaOH溶液改性沸石,1 mol·L^(-1) NaOH溶液浸泡改性的沸石同样增大沸石的比表面积和吸氨量,比表面积为21.93 m^(2)·g^(-1),吸氨量为154.4 mmol·(100 g)^(-1),但改性效果相对于NaCl和HCl改性溶液较差。沸石经100、200℃预热后再改性或改性后再经过350℃高温干燥均会降低其吸氨量。The Beipiao area in Liaoning province is rich in zeolite resources,but the level of processing and utilization is relatively low for a long time.In order to improve its specific surface area and ammonia absorption properties,different methods were used to modify zeolite.The specific surface area was measured using a specific surface area analyzer and the ammonia absorption was titrated using chemical methods.The results showed that the ammonia absorption of zeolite modified with 1 mol·L^(-1) NaCl solution for 20 h could reach 182.1 mmol·(100g)^(-1),with a specific surface area of 16.499 m^(2)·g^(-1);the zeolite modified by HCl solution had good specific surface area of 63.577 m^(2)·g^(-1) and ammonia absorption capacity of 162.9 mmol·(100g)^(-1) when soaked in 1.5 mol·L^(-1) HCl solution;modification of zeolites with 1 mol·L^(-1) NaOH solution also increased the specific surface area and ammonia absorption of the zeolite,with specific surface area of 154.4 m^(2)·g^(-1) and ammonia absorption of 154.4 mmol·(100g)^(-1).However,the modification effect was relatively poor compared to salt and acid solutions.Zeolite preheated at 100℃ or 200℃ before modification or modified and then dried at 350℃had low ammonia absorption capacity.

关 键 词:沸石 比表面积 吸氨量 预热 

分 类 号:TQ424.2[化学工程]

 