罩式退火钢卷边部氧化原因分析及控制  

Analysis and Control of Oxidation Defects at the Edge of Cover Annealing Steel Coils

在线阅读下载全文

作  者:李虎 腾瑞冲 魏学东 张晓 Li Hu;Teng Ruichong;Wei Xuedong;Zhang Xiao(HBIS Group Hengshui Strip Processing Co.,Ltd.,Hengshui Hebei 053400,China;Hebei Steel Based Metal Packaging Material Technology Innovation Center,Hengshui Hebei 053400,China)

机构地区:[1]河钢集团衡水板业包装材料科技有限公司,河北衡水053400 [2]河北省钢基金属包装材料技术创新中心,河北衡水053400

出  处:《山西冶金》2024年第12期54-55,58,共3页Shanxi Metallurgy

摘  要:采用直读光谱仪、扫描电镜(SEM)、能谱仪(EDS)和辉光测试仪,研究了T2硬度马口铁基板的边部氧化色差问题。结果表明:锰元素的富集与氧化是产生边部氧化色差的主要原因。通过控制基材成分、退火前板型、还原性气氛及退火温度,可较好地解决此类问题。Spectrometer,scanning electron microscope(SEM),energy spectrometer(EDS),glow tester are used to study the edge oxidation color of T2 tempered tinplate substrate.The results show the enrichment and oxidation of manganese are the main reason for its occurrence.Such problems can be solved by controlling matrix composition,plate shape before annealing,reducing atmosphere and annealing temperature.

关 键 词:罩式退火 边部色差 选择性氧化  

分 类 号:TG156.2[金属学及工艺—热处理]

 